INFLUENCE OF LIGHT SOURCE AND CURING TIME ON SURFACE HARDNESS OF RESIN COMPOSITES

중합 광원과 중합 시간이 복합레진의 표면 경도에 미치는 영향

  • Bae, Sang-Man (Department of Pediatric Dentistry, College of Dentistry, Wonkwang Dental Research Institute Wonkwang University) ;
  • Lee, Kwang-Hee (Department of Pediatric Dentistry, College of Dentistry, Wonkwang Dental Research Institute Wonkwang University) ;
  • Kim, Dae-Eup (Department of Pediatric Dentistry, College of Dentistry, Wonkwang Dental Research Institute Wonkwang University) ;
  • Ahn, Ho-Young (Department of Pediatric Dentistry, College of Dentistry, Wonkwang Dental Research Institute Wonkwang University)
  • 배상만 (원광대학교 치과대학 소아치과학교실.원광치의학연구소) ;
  • 이광희 (원광대학교 치과대학 소아치과학교실.원광치의학연구소) ;
  • 김대업 (원광대학교 치과대학 소아치과학교실.원광치의학연구소) ;
  • 안호영 (원광대학교 치과대학 소아치과학교실.원광치의학연구소)
  • Published : 2001.05.31
Download PDF
⟨ Previous Next ⟩

Abstract

The purpose of study was to compare the plasma arc light with the halogen light in compostie resin curing. Three composite resin materials(Z-100, 3M, USA; Tetric Ceram, Vivadent, Liechtenstein; SureFil, Dentsply, USA) were filled in the teflon molds (4mm in diameter and 2, 3, 4, 5mm in thickness) and cured with either the conventional low-intensity light curing unit with a halogen lamp (Optilux 360, Demetron, U.S.A.) for duration of 40 seconds or with the high-intensity light curing unit with a plasma arc lamp (Flipo, Lokki, France) for duration of 3, 6, and 9 seconds. The intensity of halogen light was about $370mW/cm^2$ and that of plasma light was about $1,900mW/cm^2$. After one week, the surface hardnesses of both the top and the bottom of the resin samples were measured with a microhardness tester(MXT70, Matsuzawa, Japan). There were significant differences in the hardness between the top and the bottom of the resin samples except the 2mm thickness samples cured by halogen light for 40s or by plasma light for 9s. There was no significant difference between the hardness values of the top surfaces of the thickness groups. The hardness values of the bottom surfaces decreased as the curing time decreased and as the thickness of resin samples increased, and the three kinds of resin composites showed similar patterns. The results suggest that the halogen light for 40 seconds might be able to cure greater depth of resin composites than the plasma light for 3, 6, or 9 seconds.

플라즈마 아크 광원을 사용하는 광중합기를 저출력 할로겐 광원을 사용하는 전통적인 광중합기와 비교 평가하기 위하여, 세 종류의 복합레진을 두께가 2, 3, 4, 5mm인 몰드에 충전하고 레진 상면을 할로겐광으로 40초간, 플라즈마광으로 3, 6, 9초간 조사한 후 레진 상면과 하면의 표면미세경도를 각각 측정하였다. 레진시편 상면의 표면경도와 하면의 표면경도 간의 차이는, 두께 2mm 시편에 할로겐광을 40초간 조사하였거나 플라즈마광을 9초간 조사한 경우들을 제외하고, 모두 유의하였다(P<0.05). 레진시편 상면의 표면경도는 전체 실험군들에서 서로 유의한 차이가 없었다. 레진시편 하면의 표면경도는 전체적으로 보아 할로겐광을 40초간 조사한 군들에서 가장 높았고 플라즈마광의 조사시간이 감소함에 따라 감소하였으며 레진시편의 두께가 증가함에 따라 감소하였다. 이상의 결과는 복합레진의 중합깊이 측면에서 볼 때 3, 6, 9초간 조사하는 고출력 플라즈마광의 중합능력이 40초간 조사하는 저출력 할로겐광의 중합능력에 미치지 못함을 시사한다.