Miscibility and Properties of Ethyl-Branched Polyethylene/Ethylene-Propylene Rubber Blends( I )
에틸 가지화된 폴리에틸렌과 에틸렌-프로필렌 고무 블렌드의 혼화성와 물성( I )
-
Cho, Ur-Ryong
(Department of Applied Chemical Eng., Korea Univ. of Technology and Education)
-
조을룡
(한국기술교육대학교 응용화학공학과)
- Published : 2001.09.30
Abstract
Ethyl-branched polyethylene[PE(2)] containing 2mole% ethyl branch and three ethylene-propylene rubbers(EPR's) haying the same ethylene(E)-propylene(P) molar ratio(E/P=50/50) with different stereoregularity, that is, random EPR(r-EPR), alternating-EPR(alt-FPR) and isotactic-alternating-EPR(iso-alt-EPR) were mixed for the investigation of their properties depending on the stereoregurarity. The three blends were immiscible at room temperature, and showed the simple additivity effect in density behavior. The melting point depression with blend composition increased in order of PE(2)/r-EPR>PE(2)/alt-EPR>PE(2)/iso-alt-EPR. In the tensile test, this blend systems have the lowest value or the breaking strength at FE(2) fraction of 0.5. This phenomenon results from the greastest separated phase morphology at this blend composition.
2몰% 에틸가지를 포함하는 에틸 가지화 폴리에틸렌[(PE(2)]과 에틸렌-프로필렌 몰비가 50:50으로 같지만 입체규칙성이 서로 다른 랜덤-에틸렌-프로필렌 고무(r-EPR), 교호-에틸렌-프로필렌 고무(alt-EPR) 및 이소탁틱-교호-에틸렌-프로필렌 고무(iso-alt-EPR)를 에틸렌-프로필렌 고무의 입체규칙성에 대한 혼화성과 물성의 차이를 조사하기 위하여 혼합하였다. 이 세가지 블렌드들은 상온에서 상호간에 혼화성이 없었고, 밀도 측정에서 단순한 첨가 효과를 보여 주었다. 블렌드 조성에 따른 폴리에틸렌의 녹는점 감소는 PE(2)/r-EPR>PE(2)/alt-EPR>PE(2)/iso-alt-EPR의 순서로 증가하였다. 인장시험에서 이 블렌드계는 혼합 조성이 50:50 일때 가장 낯은 파난강도의 값을 보여 주어 이 블렌드 조성에서 두 고분자 상(phase)이 가장 분리된 형태학(morphology)을 가지고 있음을 알았다.