Evaluation For Adhesion in Tension of SBR Polymer Modified Concrete Tensile by Uniaxial Method

직접인장방법에 의한 SBR 폴리머 개질 콘크리트의 부착강도 특성 평가

In this research, evaluation of adhesion in tension property of SBR-modified concrete to ordinary portland cement concrete was conducted with uniaxial direct tensile bond test which was proposed by Kuhlmann. A test set-up was fabricated in order to minimize the eccentric force by introducing a joint which might fully rotate. The main experimental variables were cement-latex ratios, surface preparations and moisture levels. The results obtained were as follows: The LMC specimen at 15% latex-cement ratio increased the adhesion in tension by range of 37% compared to that of conventional cement concrete. This might be due to latex film formed between cement paste and aggregate. The effects of surface preparation on bond of latex modified concrete to conventional concrete were significant at the conditions by sand paper and wire brush. A better bond could be achieved by rough surface rather than smooth. The saturated and surface dry (SSD) condition were considered to be the most appropriate moisture level followed by wet, finally by dry. Thus, a proper surface preparation and moisture level are quite necessity in order to obtain better bonding at LMC overlay.

본 연구는 일반 콘크리트와 SBR 라텍스 개질 콘크리트의 부착강도 특성을 분석하고자 신 구 콘크리트로 구성된 직접인장 시험체를 제작하여 부착강도를 측정하였다. 이때, 시험체와 측정기의 연결장치가 $360^{\circ}$ 회전이 가능하도록 시험장비를 개선하여 시험체의 편심이 부착강도 측정에 미치는 영향을 최소화였다. 주요 실험변수로는 라텍스 혼입율, 표면 처리상태, 표면 함수상태로 정하였으며 실험결과는 다음과 같다; 라텍스 혼입률이 증가함에 따라 부착강도도 증가하였으며, 혼입률 15%에서 37%의 증진을 보였다. 이것은 라텍스가 골재와 시멘트 페이스트 사이에 충전되어 필름 막을 형성하고 부착력을 증진시켰기 때문인 것으로 판단된다. 표면처리에 따라 부착강도의 변화를 고찰한 결과, 샌드 그라인딩과 와이어 부러쉬에 의해 표면처리를 하였을 경우 부착강도는 단순 절단한 경우보다 약 49% 증가하였다. 표면함수 상태에 따른 영향을 고찰한 결과, 부착강도는 기존 콘크리트 표면이 건조하였을 경우에 가장 작게 나타났고, 자유수가 표면에 있을 때가 그 다음을 나타냈으며, 표면건조포화상태에선 37% 증가하여 가장 크게 나타났다. 따라서 부착강도를 증진시키기 위해서는 적절한 표면처리와 표면함수상태의 유지가 필수적임을 알 수 있었다.