Abstract
The structure of the lithium zinc borate LiZnBO3 has been established by single-crystal X-ray diffraction methods. It crystallizes in the triclinic space group P1(Z=2), with unit-cell parameters - $a=5.0915(9)\AA$, $b=5.059(1)\AA$, $c=6.156(1)\AA$, $V=120.6(1)\AA3$ , $\alpha=65.81(1)^{\circ}$, $\beta=65.56(1)^{\circ}$ and $\gamma=59.77(1)^{\circ}$. The structure was determined from 704 unique reflections and refined to the final residuals R=0.039 and wR=0.056. It is characterized by an association of BO3 triangles and LiO4 and ZnO4 tetrahedra. The Li and Zn atoms are disordered around the average positions between Li1 and Li2 atoms or between Zn1 and Zn2 atoms. The disorder can be described by four half-occupied positions about Li1, Li2, Zn1 and Zn2 atoms.
LiZnBO3 화합물의 결정구조에 대한 실험은 단결정 X-ray 회절 분광법에 의해서 수행되었다. 화합물의 단위포 격자상수는 $a=5.0915(9)\AA$, $b=5.059(1)\AAc=6.156(1)\AA$, $V=120.6(1)\AA3$, $\alpha=65.81(1)^{\circ}$, $\beta=65.56(1)^{\circ}$와$\gamma=59.77(1)^{\circ}$이고, 공간 그룹은 P1(Z=2)이다. 화합물의 구조는 704개의 독특한 반사 복사선들에 의해서 결정되었으며, 최종, R값은 0.039이고, wR값은 0.056이다. 이 화합물은 평면삼각형의 BO3그룹과 찌그러진 사면체 구조의 Li04와 ZnO4그룹으로 구성되었으며, Li 원자와 Zn 원자들이 불연속적으로 배열되었다. 번갈아 가면서 불연속적으로 배열된 원자의 충진율은 각각 원자들, Li1, Li2, Zn1 와 Zn2 격자위치에서 약 50%이었다.