Enhancement of photoluminescence and electrical properties of Ga doped ZnO thin film grown on $\alpha$-$Al_2O_3$(0001) single crystal substrate by RE magnetron sputtering through rapid thermal annealing

RF 마그네트론 스퍼터링 법으로 사파이어 기판 위에 성장시킨 ZnO: Ga 박막의 RTA 처리에 따른 photoluminescence 특성변화

  • 조정 (한국과학기술연구원 박막기술연구센터) ;
  • 나종범 (한국과학기술연구원 박막기술연구센터) ;
  • 오민석 (한국과학기술연구원 박막기술연구센터) ;
  • 윤기현 (연세대학교 세라믹 공학과) ;
  • 정형진 (한국과학기술연구원 박막기술연구센터) ;
  • 최원국 (한국과학기술연구원 박막기술연구센터)
  • Published : 2001.10.01

Abstract

$Ga_2O_3$(1 wt%)-doped ZnO(GZO) thin films were grown on ${\alpha}-Al_2O_3$ (0001) by rf magnetron sputtering at $510^{\circ}C$, whose crystal structure was polycrystalline. As-grown GZO thin film shows poor electrical properties and photoluminescence (PL) spectra. To improve these properties, GZO thin films were annealed at 800-$900^{\circ}C$ in $N_2$atmosphere for 3 min. After the rapid thermal annealing(RTA), deep defect-level emission disappears and near-band emission is greatly enhanced. Annealed GZO thin films show very low resisitivity of $2.6\times10^{-4}\Omega$/cm with $3.9\times10^{20}/\textrm{cm}^3$ carrier concentration and exceptionally high mobility of 60 $\textrm{cm}^2$/V.s. These improved physical properties are explained in terms of translation of doped-Ga atoms from interstitial to substitutional site.

RF마그네트론 스퍼터링법으로 사파이어 기판 위에 Ga을 1 wt% 첨가한 ZnO 박막(GZO)을 기판온도 $550^{\circ}C$에서 성장시켜 다결정 박막을 제조하였다. 이러한 박막은 불충분한 전기적 특성이나 PL(Photoluminescence) 특성을 보이고 있다. 이러한 전하농도, 이동도 그리고 PL특성 등과 같은 전기적 광학적 특성을 향상시키고자 질소분위기하에서 RTA(Rapid Thermal Annealing) 법으로 $800^{\circ}C$$900^{\circ}C$에서 각각 3분씩 후열처리 하였다. RTA법으로 후열처리한 GZO박막의 비저항은 $2.6\times10^{-4}\Omega$/cm 였으며 전자농도와 이동도는 각각 $3.9\times10^{20}/\textrm{cm}^3$과 60 $\textrm{cm}^2$/V.s 였다. 이러한 물리적 성질들의 향상은 열처리시 원자 크기가 비슷한 도핑된 Ga 원자들이 일부 휘발되는 Zn 빈자리로 치환하면서 침입자리 보다는 치환자리로의 전이에 기인한 것으로 생각된다.

Keywords

References

  1. J. Cryst. Gowth v.216 Y. R. Ryu;S. Zhu;D. C. Look;J. M. Wrobel;H. M. Jeong;H. W. White
  2. Jpn. J. Appl. Phys. v.38 M. Joseph;H. Tabata;T. Kawai
  3. Jpn. J. Appl. Phys. v.36 K. Minegishi;Y. Koiwai;Y. Kikuchi;K. Yano;M. Kasuga;A. Shimizu
  4. Appl. Phys. Lett. v.76 T. Aoki;Y. Hatanaka;D.C. Look
  5. J. Cryst. Growth v.223 X. L. Guo;H. Tabata;T. Kawai
  6. Inorg. Mater. v.33 A. N. Georgobiani;M. B. KotlyarevskiiV. V. Kidalov;I. V. Rogozin
  7. Solar Energy Mater. Solar Cells v.49 B. Sang;A. Yamada;M. Konaghi
  8. Jpn. J. Appl. Phys. v.24 T. Minami;H. Sato;H. Nanto;S. Takata
  9. J. Appl. Phys. v.81 K. H. Kim;K. C. Park;D. Y. Ma
  10. J. Appl. Phys. v.83 R. Cebulla;R. Wendt;K. Ellmer
  11. J. Vac. Sci. Technolo. v.A15 K. Tominaga;N. Umezu;I. Mori;T. Ushiro;T. Moriga;I. Nakabayashi
  12. Thin Solid Films v.283 B. M. Ataev;A. M. Bagamadova;V. V. Mamedov
  13. Thin Solid Films v.260 B. M. Ataev;A. M. Bagamadova;A. M. Djabrailov;V. V. Mamedov;R. A. Rabadadoc
  14. J. Appl. Phys. v.72 J. Ju;R. G. Gordon
  15. J. Non-Crys. Solid v.218 Miyazaki;K. Sato;A. Mitsui;H. Nishimura
  16. Thin Solid Films v.193;194 B. H. Choi;H.B. Im;J. S. Song;K. H. Yoon
  17. Thin Solid Films v.213 D. H. Zhang;D. E. Brodie
  18. J. Appl. Phys. v.87 K. K. Kim;J.-H. Song;H. J. Jung;S.-J. Park;J. H. Song;W. K. Choi
  19. J. Vac. Sci. Technol. v.A18 no.6 K. K. Kim;J.-H. Song;H. J. Jung;S.-J. Park;J. H. Song;J. Y. Lee;W. K. Choi
  20. Elements of X-ray Diffraction B. D. Cullity
  21. J. Appl. Phys. v.84 S. A. Studeniken;N. Geoego;M. Cocivera
  22. J. Appl. Phys. v.84 Y. Chen;D. M. Bagnell;H. J. Koh;K. T. Park;K. Hiraga;Z. Zhu;T. Yao
  23. J. Cryst. Growth v.184;185 D. M. Bagnell;Y. F. Chen;M. Y. Shen;Z. Zhu;T. Goto;T. Yao
  24. J. Chem. Phys. v.80 L. E. Brus
  25. J. Appl. Phys. v.32 R. E. Dietz;J. J. Hopfield;D. G. Thomas
  26. Phys. Status Solid v.A66 E. Ziegler;A. Heinrich;H. Oppermann;G. Stover
  27. Thin solid films v.193;194 B. H. Choi;H. B. Im
  28. Solid State Commun v.105 D. C. Look;D. C. Reynolds;J. R. Stzelove;R. L. Jones;C. W. Litton;G. Cuntwalt;W. C. Harshi