Synthesis and Adsorption Characterization of Amidoximated Hydrolyzed Extruded PAN

친수성기를 부여한 아미독심화 압출 PAN 킬레이트수지의 製造 및 轉移金屬($CU^{2+}, Ni^{2+}$)의 選擇的 吸着特性 調査

Several hydrolyzed extruded PAN's were prepared through reaction of extruded PAN (7.5% methyl acrylate) with NaOH in methanol at various temperatures and times. These were amidoximated with hydroxylamine in MeOH and/or $H_2$O to introduce an excellent adsorption capacity of heavy metal ions. Amidoximated hydrolyzed extruded fAN showed superior swellability to non-hydrolyzed extruded PAM. The amidoximated extruded PAN hydrolyzed for 6h at $60^{\circ}C$ showed the best dimensional stability. Amidoximated hydrolyzed extruded PAN has more adsorption capacity of $Cu^{2+}$ than that of $Ni^{ 2+}$ These PAN derivates also showed an excellent selectivity for adsorption of metal ions.

7.5%의 methyl acrylate가 함유된 압출 PAN(polyacrylonitrile)을 NaOH와 함께 메탄올상에서 다양한 온도와 시간으로 반응을 시켜 친수성이 부여된 압출 PAN을 제조하였다. 이 PAN들을 hydroxylamine과 함께 메탄올과 수용액 상에서 반응시켜 금속이온에 대해 최적의 흡착특성을 가지는 아미독심기를 부여하였다. 친수성이 부여된 아미독심화 압출 PA처은 친수성이 부여되지 않은 압출 PAN에 비하여 우수한 팽윤성를 보였다. 친수성이 부여된 아미독심화 압출 PAN은 $60^{\circ}C$, 6시간 동안 아미독심화 시켰을 때 가장 안정한 형태를 유지하였다. 친수성이 부여된 아미독심화 압출 PAN은 $Ni^{2+}$ 보다는 $Cu^{2+}$ 에 대해 높은 흡착능을 보였으며 또한 금속이온들에 대해 높은 선택성을 나타내었다.