Degradation Behavior of PVC Film in Aqueous Solution at Elevated Temperatures

高溫 水溶液 중에서 PVC필름의 分解擧動

  • Shin, Shun-Myung (Institute of Industrial Technology Chang-won University) ;
  • Kim, Jong-Hwa (Dept. of Chemical Technology College of Engineering Chang-won University) ;
  • Lee, Soo (Institute of Industrial Technology Chang-won University)
  • 신선명 (창원대학교 산업기술연구소) ;
  • 김종화 (창원대학교 공업화학과) ;
  • 이수 (창원대학교 산업기술연구소)
  • Published : 2001.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

The heat treatment of PVC film containing PVC 65ft, DOP (Dioctyl Phthalate) 32% as plasticizer, Ca-Zn stearates and sur-face agent was performed under several conditions to study the dehydrochlorination of PVC and char production. In the case of $H_2$ $SO_4$, the dehydrochlorination was ca.100% at $250^{\circ}C$ for 3h. The char involving the smaller pores was produced with hydro-thermal treatment. The pore size became small with increasing the treatment time and temperature. In the case of treatment with $Ca(OH)_2$, the sizes of pores produced in char were about sever ~10 $\mu\textrm{m}$ at$ 225^{\circ}C$ for 12h. In the case of $_2$$SO_4$, the size of pores were about 1 $\mu\textrm{m}$ in 5M $_H2$$SO_4$for 12h.

폴리염화비닐(PVC) 64.5%, 프탈산디옥틸(DOP) 32.2%, 칼슘-아연 스테아린산 안정제 및 계면활성제 등으로 되어진 PVC 필름을 $H_2O$, $Ca(OH)_2$ 그리고 $H_2$$SO_4$용액중에서 반응온도 $200-250 ^{\circ}C$, 반응시간 0-12시간으로 수열처리하였을 경우 PVC의 탈염화수소 및 생성되는 탄소질에 관해서 조사했다. $ H_2$ $SO_4$의 경우에는 탈염화수소가 빨라 25$0^{\circ}C$, 3시간 이상에서는 탈염화수소율이 거의 100%에 도달했다. 또한 이들의 수열처리에서는 다공질의 탄소질이 생성되었고 온도가 높을수록, 그리고 반응시간이 길수록 이들의 세공경은 작아졌다. $Ca(OH)_2$의 경우에는 $225^{\circ}C$, 12시간에서는 약 5-10 $mu extrm{m}$정도의 세공이 생성되었다. 그리고 $H_2$$_SO4$의 경우에는 5M의 $_H2$$SO _4$로 12시간 처리하였을 경우 약1 $\mu\textrm{m}$정도가 되었다