Abstract
In order to analyze the photodegradation of plastic materials for floats or frames of fisheries facilities, weathering experiment on 3 kinds of plastic materials like high density PE of Korea(KHDPE) and Norway(NHDPE) and high strength PVC(Hi-PVC) was carried out during 900 hours exposure by using xenon light source of weather-Ometer. The results obtained are as follows; With increasing of ultraviolet radiation(UVR) time, a remarkable losses in the mechanical properties of each specimen were observed except for the remaining strain of HDPE materials. As NHDPE lost almost 15% of its initial tensile stress during a 900 hours exposure followed by KHDPE 12% and Hi-PVC 6%. In addition, the remaining tensile stress RS(kg/$mm^2$) decreases almost linearly with the lapse of exposure time to light Y(Year) and the empirical equations of each specimen computed as follows; KHDPE : RS=2.6769-0.0003Y($r^2$=0.63) Hi-PVC : RS=5.3470-0.0003Y($r^2$=0.91) NHDPE : RS=2.4929-0.0004Y($r^2$=0.97) It was observed by scanning electron microscope that all specimens with UVR time had started to decompose and had bubbled areas and small holes.
수산 시설물의 내구성을 평가하기 위한 기초 단계로 부력재 또는 프레임용 재질로 많이 사용되고 있는 국산 고밀도 PE 및 고강도 PVC와 노루웨이 고밀도 PE에 대하여 인공 광원을 조사한 후 시간의 경과에 따른 시료의 물성과 그 표면 및 파면의 형태적 변화를 비교$\cdot$분석하였다. 실험에서 얻어진 결과를 요약하면 다음과 같다. 1) 자외선 조사 시간이 경과됨에 따라 세 시료 모두 인장 응력과 탄성률은 미처리된 초기의 그것보다 크게 감소하였으나, 파단 신장률의 경우 처음에는 증가하다가 다시 감소하는 불규칙적인 경향을 나타내었다. 2) 잔여 응력 RS(kg/mm 상(2))와 자외선 폭로 기간 Y(Year)와의 상관 관계는 다음과 같이 나타났다. KHDPE : RS=2.6769-0.0003Y(r 상(2)=0.63) Hi-PVC : RS=5.3470-0.0003Y(r 상(2)=0.91) NHDPE : RS=2.4929-0.0004Y(r 상(2)=0.97) 3) 전자 현미경 촬영 결과, 자외선의 영향으로 시료의 표면에 물방울 형상이 나타났으며, 자외선 조사 시간이 경과됨에 따라 분자 구조의 분해로 인하여 작은 구멍이 확인되었다.