Abstract
The effects of chromium addition on the catalytic activity of Raney nickel in alkaline fuel cell (AFC) have been studied. When the catalysts are prepared from various contents of chromium, the electrochemical characteristics shows the highest mass activity of 3.588 A/g. Operating temperature and electrolyte concentration of half cell were $80^{\circ}C$ and 6N KOH, respectively. With the addition of chromium, the particle size is diminished from 12.11 $\mu\textrm{m}$ to 11.07 $\mu\textrm{m}$ and the decrease of particle size contributes to the enlargement of the specific surface area from 0.653 $\m^2$/g to 0.685$\m^2$/g. The residual aluminium contents of Raney nickel surface are considerably influenced by the particle size and chromium acts as sintering inhibitor.
크롬의 첨가에 따른 Raney 니켈의 특성을 파악하여 우수한 성능을 나타낼 수 있는 알칼리형 연료전지용 수소극의 촉매를 제조하였다. 또한 제조된 촉매를 이용, 실제 전극으로 제작하여 전류밀도를 측정한 뒤 최적의 전극재료의 제조조건을 확립하였다. 먼저 Ni-Al합금 제조시 크롬의 첨가량을 달리하여 Raney 니켈을 제조한 뒤 이를 이용하여 수소극을 제작, 전기화학적 특성을 고찰한 결과 크롬 첨가량이 증가함에 따라 mass activity도 증가하여 크롬 첨가량이 1 wt% 인 경우 최고 3.688 A/g을 나타내었다. 전기화학적 측정시 half cell의 운전온도는 8$0^{\circ}C$이었으며 전해질은 6N KOH이었다. Raney 니켈 촉매의 입자크기와 비표면 적을 조사한 결과 크롬의 첨가량이 증가함에 따라 Raney 니켈 촉매의 입자크기는 12.11 $\mu\textrm{m}$에서 크롬의 첨가량이 1.25 wt%인 경우 11.07 $\mu\textrm{m}$로 감소하였고 비표면적은 0.653 $\m^2$/g에서 0.685 $\m^2$로 중가함을 알 수 있었다. 평균입자 크기가 커짐에 따라 잔존 알루미늄의 함량은 증가함을 알 수 있었다.