Nondestructive Evaluation and Microfailure Mechanisms of Single Fibers/Brittle Cement Matrix Composites using Electro-Micromechanical Technique and Acoustic Emission

Electro-Micromechanical 시험법과 Acoustic Emission을 이용한 단섬유/시멘트 복합재료의 미세파괴 메커니즘과 비파괴적 평가

  • 박종만 (경상대학교 응용화학공학부/고분자공학전공, 항공기부품기술연구센터) ;
  • 이상일 (경상대학교 응용화학공학부/고분자공학전공, 항공기부품기술연구센터) ;
  • 김진원 (경상대학교 응용화학공학부/고분자공학전공, 항공기부품기술연구센터) ;
  • 윤동진 (한국표준과학연구원 비파괴평가그룹)
  • Published : 2001.06.01

Abstract

Interfacial and microfailure properties of the modified steel, carbon and glass fibers/cement composites were investigated using electro-pullout test under tensile and compressive tests with acoustic emission (AE). The hand-sanded steel composite exhibited higher interfacial shear strength (IFSS) than the untreated and even neoalkoxy zirconate (Zr) treated steel fiber composites. This might be due to the enhanced mechanical interlocking, compared to possible hydrogen or covalent bonds. During curing process, the contact resistivity decreased rapidly at the initial stage and then showed a level-off. Comparing to the untreated case, the contact resistivity of either Zr-treated or hand-sanded steel fiber composites increased to the infinity at latter stage. The number of AE signals of hand-sanded steel fiber composite was much more than those of the untreated and Zr-treated cases due to many interlayer failure signals. AE waveforms for pullout and frictional signals of the hand-sanded composite are larger than those of the untreated case. For dual matrix composite (DMC), AE energy and waveform under compressive loading were much higher and larger than those under tensile loading, due to brittle but well-enduring ceramic nature against compressive stress. Vertical multicrack exhibits fur glass fiber composite under tensile test, whereas buckling failure appeared under compressive loading. Electro-micromechanical technique with AE can be used as an efficient nondestructive (NDT) method to evaluate the interfacial and microfailure mechanisms for conductive fibers/brittle and nontransparent cement composites.

인장 및 압축 하중하에서 electro-pullout 시험법과 음향방출법을 이용하여, 표면 처리된 steel fiber. 탄소 그리고 유리 섬유/시멘트복합재료의 계면 물성과 미세파괴구조를 평가하였다. 기계적 interlocking을 증가시킨 steel fiber 복합재료의 계면전단강도가 미처리 또는 neoalkoxy zirconate (Zr) 처리된 steel fiber 복합재료보다 더 향상되었음을 보여주었다. 이것은 존재 가능한 수소결합 또는 공유결합에 비해 기계적 interlocking이 계면 물성에 더 많은 영향을 주기 때문으로 고찰된다. 시멘트복합재료를 경화하는 동안에, 접촉 저항도는 초기에는 급격히 감소하였으나, 이후 증가치가 둔화되는 현상을 보였다. Zr-처리 및 기계적 interlocking을 향상시킨 steel fiber 복합재료의 접촉저항은 미처리의 경우에 비해 더 나중 단계에서 무한대로 증가하였다. 기계적 interlocking이 향상된 steel fiber 복합재료의 계면 파괴에 의한 음향방출 신호의 수가 미처리 또는 Zr 처리된 복합재료에 비해 휠씬 많이 나타났다. 기계적 맞물림이 향상된 복합재료의 pullout과 마찰신호에 대한 응향방출 파형이 미처리에 비해 크게 나타났다. Dual matrix composite (DMC)에서, 압축하중 하에서의 음향방출 에너지와 파형이 인장하중 하에서의 에너지와 파형에 비해 더 크게 나타났는데, 이것은 시멘트 복합재료가 압축응력을 잘 견디는 세라믹 성질에 기인한 것으로 고찰된다. 유리섬유 복합재료의 인장 시험에서는 수직균열이 나타났고, 반면에 압축 시험에서는 buckling 균렬현상이 관찰되었다. Electro-micromechanical 시험법과 음향방출법은 전도성 섬유가 보강된 불투명한 취성기지 복합재료의 계면 물성과 미세 파괴구조를 평가하기 위한 효율적인 비파괴시험법으로 사용될 수 있다.5}$ 이상의 수준으로 가장 높게 나타났고, 그 외 다른 나라들의 경우는 $10^{4}$이상의 수준으로 유사한 수준을 나타내었다. 대장균군의 경우 미국산과 한국산, 중국산이 다소 높은 경향을 보였다.다.농도와 세포의 건조질량이 각각 $0.98$\times$10^{6}$ / cell /mL 와 0.2 g/L astaxanthin의 농도는 1.92 mg/L 단위 세포당 astaxanthin 농도는 9.6 mg/g cell 로 관찰되었다결론적으로 질소원과 peptone이 고갈되면 세포의 생장은 억제되나 astaxanthin의 생산은 촉진됨을 알수 있었으며 세포 생장을 촉진하는 광도 60$\mu$E/($\m^2$s)와 HKM 배지 이용의 1단계와 높은 광도와 MBBM배지를 이용한 색소 생산의 2단계 배양을 최적조건으로 수립하였다.내어 생채내의 free radical에 의한 간보호 작용이 있는 생리활성 물질을 함유하고 있음이 추정되며, 아울러 이 분획물을 더욱 분리하여 물질의 구조와 반응 기전 제시와 함께 간 손상의 예방 및 치료에 도움이 될 수 있는 물질을 개발할 가치가 있다고 사료된다을 공급한 대조구에 비해 높았다. 어미의 성 성숙 및 산란은 두 번의 실험에서 대조구보다 저염분구에서 원만히 이루어졌다. 암컷 성숙 개체의 경우 1차 실험은 대조구 6마리, 저염분구 12마리였으며, 2차 실험은 대조구 5마리, 저염분구 12마리였으며, 2차 실험은 대조구 5마리, 저염분구 14마리로서 성숙유도에 있어 염분의 조절에 의한 성숙이 이루어진 것을 알 수 있다. 산란 시기는 1차 실험에서 대조구나 저염분구의 산란 개시 시점이 거의 동일한 데 비해, 2차 실험에서는 저염분구가 대조구에 비해 대략 20일 정도 빠르게 나타났다. 또한 산란에 가입한 암컷 어미의 개체수도 두 차례의

Keywords

References

  1. Acta Metall. v.47 A new fracture mechanics model for multiple matrix cracks of SiC fiber reinforced brittle-matrix composites Okabe, T.;Takeda, N.;Komotori, J.;Shimizu, M.;Curtin, W. A.
  2. J. Compos. Mater. v.33 Interfacial debonding in fiber reinforced cement-matrix composites Shannag, M.;Hansen, W.;Tjiptobroto, P.
  3. J. Am. Ceram. Soc. v.74 Theory of mechanical properties of ceramic-matrix composites Curtin, W. A.
  4. Acta Mater. v.48 Tough-to-brittle transitions in ceramic-matrix composites with increasing interfacial shear stress Xia, Z.;Curtin, W. A.
  5. Acta Metall v.46 Modeling brittle and tough stress-strain behavior in unidirectional ceramic matrix composite Curtin, W. A.;Ahn, B. K.;Takeda, N.
  6. J. Am. Ceram. Soc. v.73 Influence of interfacial shear stress on first-matrix cracking stess in ceramic-matrix composites Singh, R. N.
  7. J. Mater. Sci. v.20 Interfacial effects in carbon-epoxies: Part 2. Strength and modulus with short random fibers Sanadi, R.;Piggott, M. R.
  8. J. Mater. Sci. Lett. v.12 Interfacial shear strength evaluation of ceramic-coated carbon fibers Pitkethly, M. J.;Doble, J. B.;Jacques, P.
  9. Mater. Sci. Eng. v.21 The effect of polymeric matrix mechanical properties on the fiber-matrix interfacial shear strength Drzal, L. T.
  10. Compos. Sci. & Technol. v.59 A study of interfacial aspects of epoxy-based composites reinforced with dual basalt and SiC fibres by means of the fragmentation and acoustic emission techniques Park, J. M.;Shin, W. G.;Yoon, D. J.
  11. Acta Metall. v.31 The mechanics of matrix cracking in brittle-matrix fiber composite Marshall, D. B.;Cox, B. N.;Evans, A. G.
  12. J. Adhesion v.31 New single fiber/resin interface test for highly cross-linked resin systems Lee, S. M.;Holguin, S. A.
  13. J. Mater. Sci. v.25 Stress transfer by shear in carbon fibre model composites. Part 1. Results of single-fiber fragmentation tests with thermosetting resins Favre, J. P.;Jacques, D.
  14. Polym. Compos. v.20 Interfacial properties of glass fiber/brittle-ductile dual matrix composites using micromechanical thchniques and acoustic emission Lee, S. I;Park, J. M.;Shin, D. W.;Yoon, D. J.
  15. Compos. Sci. & Technol. v.59 Experiments to relate carbon-fibre surface treatments to composite mechanical properties Ageorges, C.;Friedrich, K.;Ye, L.
  16. Composite v.30 Single fiber Broutman test: fiber-matrix interface transverse debonding Ageorges, C.;Friedrich, K.;Schuller, T.;Lauke, B.
  17. Pro. R. Soc. Lond. v.A452 The compressive fragmentation phenomenon: using microcomposites to evaluate thermal stresses, single fibre compressive strengths, Weibull parameters and interfacial shear strenghs Wood, J. R.;Wagner, H. D.;Marom, G.
  18. Compos. Interf. v.5 Thermal Shrinkage induced compressive fragmentation in composite materials Saado, Y.;Wood, J. R.;Marom, G.
  19. App. Compos. Mater. v.4 Determining the interfacial shear strength in the presence of transcrystallinity in composites by the single-fiber microcomposite compressive fragmentation test Wood, J. R.;Marom, G.
  20. Proc. ICCM-12 Electric resistance and acoustic emission during cyclic tensile loading of CFRP laminates Prasse, T.;Michel, F.;Mook, G.;Schulte, K.;Bauhofer, W.
  21. J. Mater. Sci. Lett. v.13 Acoustic emission monitoring of damage using high ampligude gains in carbon fiber reinforced poly(ether ether ketone) Verma, R. K.;Kander, R. G.;Hsiao, B. S.
  22. Polym. Compos. v.19 Interfacial properties of two SiC fiber-reinforced polycarbonate composites using the fragmentation test and acoustic emssion Park, J. M.;Chong, E. M.;Yoon, D. J.;Lee, J. H.
  23. J. Coll. Interf. Sci. v.231 Interfacial aspects of electrodeposited carbon fiber-reinforced epoxy composites using monomeric and polymeric coupling agents Park, J. M.;Kim, Y. M.;Kim, K. W.;Yoon, D. J.
  24. Proc. ICCM-12 Smart NDT using electrical resistance method for delamination monitoring in CFRP Yuse, K.;Bathias, C.
  25. Compos. Interf. v.4 Single-fiber electromechanical pull-out testing and its application to studying the interface between steel fiber and dement Fu, X.;Chung, D. D. L.
  26. Cem. Conc. Res. v.25 Linear correlation of bond strength and contact the electrical resistivity between steel rebars and concrete Fu, X.;Chung, D. D. L.
  27. Cem. Conc. Res. v.26 Improving the bondstrength between carbon fiber and cement by fiber surface treatment and polymer addition to cement mix Fu, X.;Chung, D. D. L.
  28. Cem. Conc. Res. v.25 Contact the electrical resistivity between cement and carbon fiber: its decrease with increasing bond stregth and its increase during pullout Fu, X.;Chung, D. D. L.
  29. Compos. Interf. v.5 Residual stress in carbon fiber embedded in epoxy, studied by simultaneous measurement of applied stress and electrical resistance Wang, X.;Chung, D. D. L.