Strength properties of arch type laminated lumber produced from domestic small lumbers

소경재를 이용한 집성 arch재의 강도 특성

This study was carried out to investigate the strength and technical feasibility of arch type laminated lumber from the domestic small lumbers(Pinus densiflora S. et Z. and Larix kampferi Catt.). Arch type lumbers manufactured with different compositions of laminae. It was designed to improve the strength and stiffness. Strength S. rt Z. U;timate load Carr. laminated lumbers were higher than that of the Pinus densiflora S. et Z. Ultimate load of 7-ply laminated lumbers were 2 times higher than the 5-ply laminated lumbers. The strength of finger jointed lumbers were found to be about 15.8% less than that of the no joint lumber. One solution for this problem is to use veneer as face lamina. The veneer laminated lumbers was considerably greater than that of the non-veneer laminated lumbers. It was suggested that this small lumber may be a candidate for high valued product member to provide the proper combination of laminae.

본 연구에서는 국산 소경제(소나무, 낙엽송)로 제작한 집성 아치재의 강도와 제작방법을 연구하였다. 아치형 집성재는 강도와 초기강성을 향상시키기 위하여 여러 가지 다른 kal나의 조합으로 제작하여 강도를 평가하였다. 실험결과 낙엽송 집성재의 rkde가 소나무 집성재보다 높게 나타났으며, 7ply 집성재의 최대하중이 5ply보다 약 2배 높은 경향을 보였다. 또한, 핑거 조인트된 라미나로 제작된 집성재는 무종접합 집성재보다 약 15.8% 낮은 강도를 나타내었다. 이 같은 문제해결의 한 방안으로 집성재의 최외각층에 베니어를 적층시켜 보강하였을 때, 베니어 집성재가 베니어로 보강하지 않은 집성재보다 월등히 높은 강도를 나타내었다. 본 연구결과 알맞은 라미나 조합으로 부재를 제작한다면 소경재의 활용이 가는하고 부가가치를 높일 수 있을 것으로 생각된다.