Abstract
Hydroxyapatite-yttria stabilized zirconia bioceramics containing fine zirconia particles were prepared as 3-layered functionally graded materials (FGMs) using a spark plasma sintering (SPS) and hot pressing (HP) apparatuses. The pretreatment of the raw hydroxyapatite promoted the sinterability of hydroxyapatite. The maximum density of pretreated FGM composites could be obtained at lower temperature than that for he untreated FGM samples. No decomposition from hydroxyapatite to three calcium phosphate (TCP) was observed in FGMs of HAp-$ZrO_2$ sintered below $1200^{\circ}C$ for 8 min under 10 MPa by SPS. However, the transformation of the tetragonal zirconia to the cubic modification had occurred in FGMs at this temperature. The presence of zirconia i.e. stress induced transformation of zirconia may be expected to enhance the mechanical properties of HAp-$ZrO_2$ FGM. The SPS is concluded as a better method to fabricated the FGM with dense and high strength compared with HP process.
수산화아피타이트와 이트리아 부분 안정화된 지르코니아의 바를 달리하는 3층 구조를 가즌ㄴ 생체 재료용 경사기능재료(FGMs)를 spark plasma sintering(SPS)과 hot pressing(HP) 장비로 제조하였다. HAp 원료에 대한 전처리를 실시할 경우 HAp의 소결성이 개선되었다. 전처리하여 얻은 FGM 복합체의 최고밀도는 전처리하지 않은 FGM 보다 낮은 온도에서 얻을 수 있었다. SPS로 FGM 소결체를 제조할 경우 10 MPa의 가압조건에서 8분 동안 소결 할 경우, $1200^{\circ}C$의 온도에서도 HAp의 TCP로의 분해 반응은 일어나지 않았으나. 이 온도에서 FGm의 지르코니아는 정방정에서 압방정으로와 상변화가 일어났다. 지르코니아 첨가에 따라. 즉 지르코니아의 응력 유기 상전이에 의해, HAp-ZrO$_2$ FGm 소결체의 기계적 물성이 증진된 것으로 예산된다. 치밀하고 고강도의 FGM을 제조하는 방법으로서 SPS가 HP공정에 비해 우수한 것으로 나타났다.