Abstract
The crystal size was determined as a function of reaction temperature, during the crystallization process of NaX zeolite. The measured rate constants for linear growth were as 0.0441$\mu\textrm{m}$/h at $80^{\circ}C$, 0.0595$\mu\textrm{m}$/h at $90^{\circ}C$ and 0.0972$\mu\textrm{m}$/h at $100^{\circ}C$, respectively. The activation energy calculated from the relation between the linear growth rate an the reaction temperature was 43.243kJ/mol. The reaction of crystal growth were revealed as 20 days at $80^{\circ}C$, 16 days at $90^{\circ}C$ and 9 days at $100^{\circ}C$, respectively. Both the final product crystal size an the crystallization time were decreased with increasing reaction temperature.
NaX 제올라이트의 결정화 과정 중 온도에 따른 결정 크기를 측정하였다. 이때 선형결정성장속도 상수는 80, 90, 100$^{\circ}C$에 대해서 각각 0.0441$\mu\textrm{m}$/h, 0.0595$\mu\textrm{m}$/h 그리고 0.0972$\mu\textrm{m}$/h로 얻어졌다. 반응온도와 선형결정성장율 사이의 관계를 이용하여 활성화에너지는 43.243 kJ/mol 로 계산되었다. 결정화 반응의 종료는 각각 $80^{\circ}C$에서 20일 90$^{\circ}C$에서 16일, 100$^{\circ}C$에서 9일로 각각 나타났다. 반응온도의 증가에 따라서 최종생성물 결정크기는 감소할 뿐만 아니라 결정화 시간도 역시 감소하였다.