Abstract
Through alkaline hydrothermal activation processes, Na-A type zeolite was synthesized as a single phase with funnel-glass waste from a television tube factory. The autoclaving was performed in a closed teflon vessel in the range of 80~95$^{\circ}$C. The silica-rich solution as a starting material was hydrothermally synthesized with quartz in IN NaOH by heating 350uC under the pressure of 1,500 atm. $NaAlO_2$ was made from NaOH and Al(OHh by heating 95$^{\circ}$C for 2-3 hours and the molar ratios of it were $Na_2O/Al_2O_3$ = 1.4 and $H_2O/Na_2O$=8. The equi-dimensional A type zeolite (1-2 11) was formed by the simple mixing of the silica-rich solution, glass waste and $NaAlO_23$ for 1-3 hours-heating at $80^{\circ}C$. The characterization of the reaction product shows Na-A as a single phase. The synthesized zeolite has cuba-dodecahedral form and $Ca^{2+}$ ion exchange capacity of the Na-A was in the range of 215-220 mequiva1entilOO g.
브라운관 후면유리 연마 후 발생되는 고상의 유리폐기물을 재활용을 위해, A형 제올라이트의 최적합성조건을 규명하고 생성된 제올라이트의 제반 특성을 기존의 상용 제올라이트와 비교하였다. 테프론 반응용기에 고규산질 알카리용액, NaAlO$_2$그리고 브라운관 유리폐기물 등 3가지 출발물질을 혼합하고, 80~95$^{\circ}C$ 범위에서 가열하여 제올라이트 Na-A를 열수조건하에서 결정화시켰다. 고규산질 알카리 용액은 자연산 규석을 35$0^{\circ}C$, 1500 기압하에서, NaAlO$_2$는 NaOH와 Al(OH)$_3$시약을 95$^{\circ}C$에서 2~3시간 가열하여 $Na_2$O/Al$_2$O$_3$=1.4, $H_2O$/$Na_2$O=8이 되도록 각각 합성하여 출발물질로 사용하였다. 브라운관 유리 폐기물과 고규산질 알카리 용액의 혼합비율 약 1:10~1:13의 범위에서 Al-공급원으로서 1.5~2.5N의 NaAlO$_2$를 혼합하였을 때 양호한 A-형 제올라이트 결정이 생성되었다. 합성된 Na-A는 하이드록시소달라이트 등과 같은 불순물이 없는 단일상이었으며, 결정형태는 입방 십이면체 (cubo-dodecahedral)형이었고 결정의 1~2 $\mu$의 균질한 입도로 분포하였다. $Ca^{+}$ 양이온교환용량은 215~220 mequivalent/100 g이었다.