Abstract
Cylindrical type ceramic filers, that is 60 O.D$\times$10t$\times$600L and 60 O.D$\times$10t$\times$1,000L were manufactured by vacuum forming processes using ceramic ray materials. For cylindrical type ceramic filters, porosity and bulk density were measured for, 80 to 90% and 0.3 to 0.4 g/㎤, respectively at uniform pore size of 41 to 45${\mu}{\textrm}{m}$. Bench scale candle filters (60$\psi$ $\times$10t$\times$600L) were tested using different dusts collected from many industries including chemical processing, glass processing and metal manufacturing pants. Collection efficiencies found out to range from 99.87% to 99.90%, while resistance coefficients from 1.1$\times$10(sup)11/$m^2$ to 1.7$\times$10(sup)11/$m^2$ . Full scale low density ceramic filters (60$\psi$ $\times$10t$\times$1,000L) were also tested at 1 atm, $600^{\circ}C$ to reveal the filtration efficiency, conditioning, and resistance coefficients using two different types of dust as chemical processing and metal refined processing. Darcys law resistance coefficients were measured to range 1.44$\times$10(sup)11/$m^2$ to 2.74$\times$10(sup)11/$m^2$, and collection efficiencies on the range 99.84 to 99.96%, Finally, results of long term performance test showed that filters were conditioned after 170hrs. Experimental conditions for effective filtration were examined under the condition 10 cm/sec face velocity, 3kg/$\textrm{cm}^2$ pulsing pressure, 5 min filtration cycle, and 300msec pulse opening time.