CHARACTERISTICS OF ELECTRICAL RESISTANCE IN MN-CO-NI-FE OXIDE

MN-CO-NI-FE 산화물의 전기저항특성

The properties of electrical resistance of Mn-Co-Ni-Fe oxide-based therrnistor with various Fe contents in sintering process at 1200 to 1400℃ for 4 hours in air atmosphere for fabricating therrnistor materials were investigated. The results were as follows: all samples showed single cubic spinel crystal structures in all region. The electrical conductivinity is the highlest thermistor sintered at 1300℃ for 4 hours. In general when the Fe content is increased except F-2, the resistivity increases and relatively the conductivity decreases. Particularly F-2 composition exhibited the highlest electrical conductivity(1.4x $10^-3$$Ω$cm) and relatively low B constant(2906K)

Mn-Co-Ni 3성분계에 Fe의 첨가량을 변화시켜 따른 산화물 서미스터소결체 (Mn-Co-Ni-Fe oxide)를 소성온도 1200 ~ 1400 에서 제조하여 전가저항특성을 조사한 결과， 결정상은 단일 입방정 스피델형 결정구조였고， 소성온도에 따른 전가전도도는 1300℃에서 4시간 소결한 서미스터가 가장 높았다. 대체로 F-2를 제외하고는 Fe의 첨가량이 증가할 때 비저항은 증가하고 상대적으로 전가전도도는 감소한다 특히 F-2의 조성에 있어서는 전가전도도가 1.4 x$10^-3$$Ω$cm로 높았고 상대적으로 B정수는 2906K로 낮았다.