Capacitance Properties of the Polypyrrole Films Electropolymerized in Different Electrolyte Solutions

전해 중합에 따른 폴리피롤 필름의 캐페시턴스 특성

  • Park Ho Chul (Department of Chemical Technology, Hanbat National University) ;
  • Noh Kun Ae (Department of Chemical Technology, Hanbat National University) ;
  • Kim Jong Huy (Korea Institute of Energy Research, Taedok Scinece) ;
  • Ko Jang Myoun (Department of Chemical Technology, Hanbat National University)
  • 박호철 (한밭대학교 응용화학공학부 공업화학과) ;
  • 노근애 (한밭대학교 응용화학공학부 공업화학과) ;
  • 김종휘 (한국에너지기술연구소) ;
  • 고장면 (한밭대학교 응용화학공학부 공업화학과)
  • Published : 2001.08.01
Download PDF
⟨ Previous Next ⟩

Abstract

Electro-conducting Polypyrrole(PPy) films were Prepared by applying constant current in various electrolytes solutions and their capacitance properties were investigated using cyclic voltammetry. Capacitance values were strongly dependent on the electrolytes solution used in electrochemical polymerization. PPy prepared in PC/AN mixture solution containing 0.5M $LiClO_4$ with small amount water showed 401 F/g and that electrogenerated in $AN/H_2O$ mixture solution containing 0.5M $LiClO_4$ retained $70\%$ of initial capacitance after 2000 cycles.

정전류법으로 다양한 전해용액에서 제조한 Polypyrrole(PPy) 필름의 캐페시턴스 특성을 cyclic voltammetry 기법을 이용하여 조사하였다. 0.5M $LiClO_4/PC(propylene carbonate)/AN(acetonitrile)$ 혼합용액에 $10\%$의 수분을 첨가한 전해질에서 제조한 PPy필름이 가장 큰 401 F/g의 커패시턴스를 나타내었다. 또한 0.5M $LiClO_4\;AN에\;10\%$의 수분을 혼합한 전해질에서 제조한 PPy필름은 2000회의 충방전에서 초기용량의 $70\%$를 나타내었다. 제조된 PPy필름의 케폐시턴스 특성은 사용된 용매에 크게 의존함을 알 수 있었다.