Analysis for Cause of Corrosion and Gas Leakage on LP-Gas Cylinder

LP가스 용기의 부식 및 가스누출 원인 분석

  • Choi S. C. (Institute of Gas Safety Technology, Korea Gas Safety Corporation) ;
  • Jo Y. D. (Institute of Gas Safety Technology, Korea Gas Safety Corporation) ;
  • Kweon J. R. (Institute of Gas Safety Technology, Korea Gas Safety Corporation) ;
  • Kim J. Y. (Institute of Gas Safety Technology, Korea Gas Safety Corporation)
  • 최송천 (한국가스안전공사 가스안전시험연구원) ;
  • 조영도 (한국가스안전공사 가스안전시험연구원) ;
  • 권정락 (한국가스안전공사 가스안전시험연구원) ;
  • 김지윤 (한국가스안전공사 가스안전시험연구원)
  • Published : 2001.03.01
Download PDF
⟨ Previous Next ⟩

Abstract

Factors to cause accidents were investigated through a systematic analysis of leakage accidents in welded LP-gas cylinder between 199 and 1999. As a result It was showed that most of leakage accident occurred at the pin-hole due to the localized corrosion on welded zone in cylinder. Accordingly, in this paper, we suggested that the problems of heat treatment condition in two-piece welded cylinder and substitute proposal for preventing the tearing of T zone in three-piece welded cylinder. Furthermore, corrosion rate on the weldment and base metal of welded LP-gas cylinder was evaluated using the electrochemical tests in acid rain and $3.5\%NaCl$ solution, Also, the poor adhesion and defects of film which was produced by electrostatic powder spray painting, while the LP-gas cylinder was manufactured, were analyzed using SEM(Scanning Electron Microscopy). And we proposed a optimum coating thickness of the cylinder.

LP가스 용접 용기의 가스 누출사고에 대한 통계적 분석을 통하여 사고 발생에 영향을 미치는 주된 요인을 조사하였다. 그 결과 대부분의 가스 누출은 용접부 국부부식에 따른 핀홀에 의한 누출이 가장 큰 비중을 차지하고 있다. 따라서, 본 논문에서는 2부구조 용기에서의 열처리조건의 문제점과 3부구조 용기의 T부위 터짐 현상에 의한 대책안을 제시하였다. 나아가, LP 가스 용기의 용접부 및 모재부에 대하여 산성비와 해수 분위기에서의 부식속도를 전기화학적 부식실험을 통하여 측정하였다. 또한, LP가스 용기의 제조공정중 분체도장 공정에 의한 도장막의 부착성 및 결함을 주사전자현미경을 통하여 분석하고 최적의 도장 두께를 제시하였다.