Abstract
Linear and star-shaped, poly(lactic acid) (PLA) stereo-block copolymers were synthesized by sequential polymerization of DL-lactic acid and L-lactide in the presence of diol or polyol compounds. The molecular weight of block copolymers could be controlled to some extent by the variation of alcohol content. These block copolymers had relatively narrow molecular weight distributions. The glass transition temperature and melting temperature of block copolymers appeared at around 5$0^{\circ}C$ and 100~14$0^{\circ}C$, respectively. The block copolymers were found to crystallize even at the high D-stereoisomer concentration of 35 mol%, in contrast to the amorphous nature of the random copolymer with similar composition. Also we could observe the crystallinity of PLA stereo-block copolymers varying with annealing temperature and time.
디올 또는 다가 알콜의 존재 하에서 DL-락트산 및 L-락티드를 연속 중합하여 선형 (ABA 형)과 스타형 ((AB)$_{n}$ 형)의 폴리락트산 입체블록 공중합체를 합성하고 분석하였다. 알콜의 함량에 따라 블록 공중합체의 분자량을 어느 정도 범위에서 조절할 수 있었으며, 합성된 중합체는 비교적 좁은 분자량 분포를 나타내었다. 폴리락트산 입체블록 공중합체의 유리전이온도는 5$0^{\circ}C$ 부근이었으며, 융점은 구조와 분자량에 따라 100~14$0^{\circ}C$ 범위에서 관찰되었다. 용융 엔탈피로부터 얻은 결정화도의 측정 결과로부터 블록구조를 갖는 공중합체는 D-입체이성질체 단량체의 높은 조성(~35%)에서도 결정화가 충분히 일어남을 확인하였는데 이는 유사한 조성의 랜덤 공중합체의 성질과 대비된다. 선형과 스타형 블록 공중합체의 경우 모두 열처리 온도와 시간에 따른 결정화도의 변화를 관찰하였다.다.