Diffusion-controlled Cure Kinetics of High Performance Epoxy/Carbon Fiber Composite Systems

확산속도에 따라 한계경화도를 갖는 에폭시/탄소섬유 복합재료의 경화반응 속도 연구

  • 박인경 (성균관대학교 고분자공학과) ;
  • 금성우 (성균관대학교 고분자공학과) ;
  • 이두성 (성균관대학교 고분자공학과) ;
  • 김영준 (성균관대학교 섬유공학과) ;
  • 남재도 (성균관대학교 고분자공학과)
  • Published : 2000.01.01

Abstract

Using a commercial epoxy/carbon fiber composite prepreg (DMS 2224) as a model system, the cure kinetics of vitrifying thermoset system were analyzed by isothermal and dynamic-heating experiments. Focusing on the processing condition of high performance composite systems, a phenomenological kinetic model was developed by using differential scanning calorimetry (DSC) and reaction kinetics theories. The model system exhibited a limited degree of cure as a function of isothermal temperature seemingly due to the diffusion-controlled reaction rates. The diffusion-controlled cure reaction was incorporated in the development of the kinetic model, and the model parameters were determined from isothermal experiments. The first order reaction was confirmed from the characteristic shape of isothermal cure thermograms, and the activation energy wes 78.43 kJ/mol. Finally, the proposed model was used to predict a complex autoclave thermal condition, which was composed of several isothermal and dynamic-heating stages.

본 연구에서는 항공기 구조용 재료로 쓰이는 탄소섬유/에폭시 복합재료 프리프레그(DMS 2224)를 모델시스템으로 하여 등온환경과 등속도 가열환경에서 경화반응 속도를 연구하였다. 이 복합재료의 공정온도에서의 가공공정을 묘사할 수 있는 현상학적인 반응속도 모델을 differential scanning calorimetry (DSC)와 이론을 통하여 제안하였다. 등온환경에서의 실험으로부터 반응특성곡선을 관찰한 결과 경화반응이 1차 반응함수임을 확인하였고, 활성화 에너지는 78.43 kJ/mo1을 얻었다. 이 프리프레그는 경화온도에 따라 한계경화도를 보여주어 유리화가 존재함을 확인하였고 이를 1차 반응속도 모델에 적용시킨 결과, 유리화 이후의 확산우세현상을 포함한 반응속도 모델을 제안하였다. 제안된 모델식을 이용하여 등온/등속도 가열환경을 포함한 실제 경화공정을 성공적으로 표현할 수 있었다.

Keywords

References

  1. Adv. Polym. Sci. v.72 R. J. Morgan
  2. Adv. Polym. Sci. v.72 J. M. Barton
  3. Polym. Eng. Sci. v.19 N. S. Schneider;J. F. Sprouse;G. L. Hangnoucer;J. H. Gillam
  4. Polym. Bull. v.1 L. Banks;B. Ellis
  5. Thermal Characterization of Poly- meric Materials R. B. Prime;E. A. Turi(ed.)
  6. J. Appl. Polym. Sci. v.29 J. Mijovic;J. Kim;J. Slaby
  7. Polym. Eng. Sci. v.27 C. S. Chern;G. W. Poehlein
  8. Polymer v.20 M. E Ryan;A. Dutta
  9. Polym. Eng. Sci. v.31 J. M. Kenny;A. Trivisano
  10. J. Appl. Polym. Sci. v.41 G. Wisanrakkit;J. K. Gillham;J. B. Enns
  11. J. Thermal Analysis v.5 J. Zsako
  12. J. Polym. Sci.: Polym. Phys. v.29 J.-D. Nam;J. C. Seferis
  13. J. Polym. Sci.: Polym. Phys. v.30 J.-D. Nam;J. C. Seferis
  14. Polym. Degra. Stab. v.19 J. S. Roman;E. L. Macdruga;L. Pargada
  15. Aspects of Degradation and Stabilization of Polymer J. H. Flynn;H. G. Jellinek(ed.)
  16. J. Appl. Polym. Sci. v.5 C. D. Doyle
  17. Thermochimica Acta v.122 C. Rozycki;M. Maciejewski
  18. J. Thermal Anal. v.11 G. I. Seum;R. T. Yang
  19. Carbon Epoxy Prepreg-Impact Resistant Douglas Aircraft Company
  20. Thermal Analysis T. Hatakeynama
  21. J. Appl. Polym. Sci. v.53 S. L. Simon;J. K. Gillham
  22. J. Appl. Polym. Sci. v.44 S. Montserrat
  23. Macromolecules v.24 A. Hale;C. W. Macosko
  24. Polym. Eng. Sci. v.13 R. B. Prime
  25. J. Appl. Polym. Sci. v.28 J. B. Enns;J. K. Gillham
  26. J. Polym. Sci.: Polym. Phys. v.25 A. T. DiBeneditto
  27. J. Appl. Polym. Sci. v.39 K. P. Pang;J. K. Gillham
  28. Polymer Letters v.B4 J. H. Flynn;L. A. Wall
  29. Anal. Chem. v.29 H. E. Kissinger
  30. J. Appl. Polym. Sci. v.50 J.-D. Nam;J. C. Seferis