Antibacterial Properties of $Ag_2-Li_2O-CaO-TiO_2-P_2O_5$Porous Class Ceramics

$Ag_2-Li_2O-CaO-TiO_2-P_2O_5$계의 다공성 글라스 세라믹스의 항균 특성

Porous glass ceramics composed of $Ag_2-Li_2O-CaO-TiO_2-P_2O_5$-CaO with 0.05-1.5 mole CuO were prepared by melting and 2 step heat treatment for nucleation at $610^{\circ}C$ and crystallization at $840^{\circ}C$. $\beta$-$Ca_3(PO_4)_2$crystal phase was selectively leached out in 1N-HC1 solution for 3 days, leaving $AgTi_2(PO_4)_3$and $LiTi_2(PO_4)_3$crystal phases. Antibacterial effects and characterizations of the porous glass ceramics were investigated. Staphylococcus aureus and Salmonella typhi bacteroa were used in this study. It was found that the resultant porous glass ceramics show excellent bacteriostatic properties.

인산염계 Ag₂OㆍLi₂OㆍCaOㆍTiO₂ㆍP₂O/sub 5/ 조성에 CuO를 0.05∼l.5 mole 첨가하여 다공성 글래스 세라믹스를 제조하였으며. 제조된 모유리는 최적 핵형성을 위해 610℃. 최고 결정성장을 위해 840℃에서 열처리하였다. 1N-HC1에서 β-Ca₃(PO₄)결정상만을 선택적으로 용출하였으며 LiTi₂(PO₄)₃상과 AgTi₂(PO₄)₃결정상이 존재하는 Glass Ceramics를 제조하였다. 다공성 글래스 세라믹스의 항균효과 및 특성을 평가하였다. Staphylococcus aureus와 Salmonella typhi 균이 본 연구에 사용되었으며, 탁월한 항균효과를 나타내는 것으로 평가되었다.