Effect of annealing pressure on the growth and electrical properties of $YMnO_3$ thin films deposited by MOCVD

Ferroelectric YMnO$_3$ thin films were deposited on $Y_2$O$_3$/si(100) substrates by metalorganic chemical vapor deposition. The YMnO$_3$ thin films annealed in vacuum ambient (100 mTorr) above 75$0^{\circ}C$ show hexagonal structured YMnO$_3$. However, the film annealed in oxygen ambient shows poor crystallinity, and the second phase as $Y_2$O$_3$ and orthorhombic-YMnO$_3$ were shown. The annealing ambient and pressure on the crystallinity of YMnO$_3$ thin films is very important. The C-V characteristics have a hysteresis curve with a clockwise rotation, which indicates ferroelectric polarization switching behavior. When the gate voltage sweeps from +5 to 5 V, the memory window of the Pt/YMnO$_3$/Y$_2$O$_3$/Si gate capacitor annealed at 85$0^{\circ}C$ is 1.8 V. The typical leakage current densities of the films annealed in oxygen and vacuum ambient are about 10$^{-3}$ and 10$^{-7}$ A/cm$^2$ at applied voltage of 5 V.