Abstract
The intercalated compounds of alkylsulfonates into hydrated zinc were synthesized. From the high temperature powder X-ray diffraction (HTXRD), FT-IR, and molecular size, the temperature dependence of orientation for the intercalated alkylsulfonates were determined. In the temperatures range 1, alkylsulfonates were intercalated into hexa aqua zinc layer with the bilayer structure of $32.9^{\circ}$angle for ${Zn(H_2O_4]^{2+}[C_nH_{2n+1}SO_3]_2\;^-$. In the temperatures range 2, alkylsulfonates were intercalated into tetra aqua zinc layer with the bilayer structure of $55.2^{\circ}$angle for ${Zn(C_nH_{2n+1}SO_3)_2$. In the temperatures range 3, alkylsulfonates were directly bonded to zinc ion with the bilayer structure of $76.5^{\circ}$angle for ${Zn(C_nH_{2n+1}SO_3)_2$.
수화된 아연에 알킬술폰이 층간 삽입된 화합물을 합성하였다. 고온 X-선 회절 데이타와 적외선 스펙트럼, 그리고 분자의 크기로 부터 층간 삽입된 알킬술폰의 공간배열의 온도 의존성을 확인하였다. 온도 구간 1에서는 ${Zn(H_2O_6]^{2+}[C_nH_{2n+1}SO_3]_2\;^-$구조를 가지며 여섯 개로 수화된 아연층에 알킬술폰이 $32.9^{\circ}$로 경사진 이중층 구조를 가짐을 확인하였다. 온도구간 2에서는 ${Zn(H_2O_4]^{2+}[C_nH_{2n+1}SO_3]_2\;^-$구조를 가지며 네개로 수화된 아연층에 알킬술폰이 $55.2^{\circ}$로 경사진 이중층 구조를 가짐을 확인하였다. 온도 구간 3에서는 알킬술폰이 아연금속에 직접 결합된 ${Zn(C_nH_{2n+1}SO_3)_2$구조를 가지고 있으며 $76.5^{\circ}$의 큰 경사각을 유지하면서 이중층 구조를 가짐을 확인하였다.