A Study on Reduction Treatment of EAF′s Dusts Mixed with Millscale

電氣爐製鋼粉塵과 millscale 混合펠릿의 還元擧動에 관한 硏究

Generally, the residues of EAF's dusts treated by reduction process at high temperature are disposed. If the residues can be recycled as iron sources of EAF by upgrading their iron contents, it can be expected to reduce the amounts of disposed wastes and the environmental impacts. Reduction of EAF's dusts mixed with millscale was carried out in rotary hearth furnace to upgrade iron contents of reduction residues. Dusts should be reduced rapidly to protect from reoxidation of reduced iron residue which can be reoxidized at high temperature. In our experimental conditions, optimum reduction time was about 40min. and iron contents of the residues were increased with increasing mixing ratio of millscale and upgrade to 85% at 50%wt mixing ratio. Zinc and lead contents in residues were about 3% and 0.5% respectively. The residues reduced rapidly must be recycled in EAF because heavy metal elements in the residues can be extracted easily and contaminate air and water.

전기로제강분진을 환원처리하여 철원으로 활용하는 경우, 매립폐기물 감소의 환경적 효과와 아울러 폐자원의 재자원화 효과가 기대된다. 본 연구에서는 제강공장에서 발생하는 millscale을 환원제와 함께 전기로제강분진에 혼합하고 회전상로에서 환원처리하여 Fe성분함량을 높이는 가능성을 조사, 검토하였다. millscale을 전기로제강분진에 혼합하여 처리함으로써 잔사 중의 Fe성분함량을 증가시킬 수 있었으며, 50 wt% millscale혼합 시 처리잔사 중의 $\boxDr$Fe성분함량은 85% 정도를 얻을 수 있었다. 회전상로에서 환원처리시 환원된 $\boxDr$Fe성분의 재산화가 일어나지 않도록 환원성분위기에서 가급적 빠른시간에 처리할 필요가 있으며 본 실험을 통하여 얻은 최적의 환원처리시간은 40분 정도이었다. 이때 잔사 중에 잔류하는 Zn및 Pb성분함량은 각각 3% 및 0.5%정도이었다. 환원성분위기에서 빠르게 처리된 경우의 처리잔사는 매립, 폐기 시 잔사 중에 함유된 금속성분들의 상당량이 용출되므로 별도의 사전처리 없이 매립, 폐기하여서는 않되며 전기로로 재투입하는 등 재활용하는 것이 바람직하다