Microwave Absorber Prepared by Using the Wasted Mn-Zn Ferrite and the Cement

Mn-Zn ferrite 廢棄物과 시멘트를 이용한 電波吸收體

The complex permeability, the complex permittivity and the reflection loss are investigated in the composite microwave absorbers which are mixed with the wasted Mn-Zn ferrite and the industrial cement. The cement has larger the complex permittivity than that of the rubber. The complex permittivity is decreasing with the increment of the mixing ratio of Mn-Zn ferrite to cement (F/C in weight) and the complex permeability is increasing with the increment of F/C. The maximum reflection loss is above -40 dB at all samples. The matching frequency is in the range of 1.3 GHz to 2.9 GHz and is decreasing with the increment of F/C from 1 to 3. The matching thickness is increasing with the increment of F/C. The wasted Mn-Zn ferrite and the cement is very useful material for the composite microwave absorber.

Mn-Zn ferrite 폐기물을 시멘트와 혼합한 복합전파흡수체를 제작하여 재료정수 및 반사감쇠량을 조사하였다. 지지재로 사용한 시멘트는 실리콘 고무의 재료정수와 비교하여 높은 복소유전율($\varepsilon$=$_{r}$': 7.6, $\varepsilon_{r}$ ": 0.6)을 나타내었고, Mn-Zn ferrite 폐기물과 시멘트의 혼합무게비(F/C)가 증가함에 따라 복소유전율은 감소하였고, 복소투자율은 증가하였다. 최대반사감쇠량을 나타내는 주파수는 F/C가 1에서 3으로 증가함에 따라 2.7 GHz에서1.3 GHz로 감소하였고, 정합두께는 8.7 mm에서 12.7 mm로 증가하는 경향이 나타났다. 모든 시편에서 최대반사감쇠량은 -40 dB 이상으로 Mn-Zn ferrite 폐기물을 전파흡수체로 활용이 가능하다.