Abstract
With the object of developing a non-gap choke core, effects of annealing in oxygen atmosphere on magnetic properties for Fe$_{78}$Si$_{9}$B$_{13}$ amorphous alloy were investigated. After annealing for 2 hrs at 440 $^{\circ}C$, optimum magnetic properties for choke core were obtained, where the effective permeability was 180 and was almost constant up to several MHz, and the decrease in permeability upon large DC bias current of 12 A or DC bias magnetic field of 8,000 A/m was very little. Moreover the AC magnetic loss was very low as compared to the conventional choke cores. Upon the optimum annealing, the magnetic hysteresis loop was inclined accompanying the increase of coercive force and the appearance of fine crystallites of $\alpha$-Fe phase. The good choke core properties was considered to be due to the suppression of domain boundary motion and domain refinement by the crystallites.
Fe$_{78}$Si$_{9}$B$_{13}$ 비정질 합금을 스위칭 전원의 평활용 쵸크 코어로 사용하기 위한 최적 열처리 조건을 조사하였다. 코어의 모양은 자기경로 상에 공극을 넣지 않는 무공극형으로 하였으며, 보다 효과적으로 쵸크 코어 특성을 얻기 위해 산화 분위기 중에서 열처리하였다. 이 합금에서 가장 양호한 쵸크 코어 특성은 44$0^{\circ}C$, 2시간의 열처리에 의하여 얻어졌으며, 그 때의 실효투자율은 180 정도로서 수 MHz의 높은 주파수 영역에 이르기까지 그 크기가 일정하게 유지되었다. 또 12A가지의 직류 바이어스 전류 또는 8,000 A/m의 직류 바이어스 자장을 가하여도 실효투자율의 저하가 나타나지 않는 우수한 직류중첩 특성을 나타내었다. 그리고 교류 자심 손실도 종래의 쵸크 코어에 비해 상당히 낮은 것으로 나타났다. 이와 같은 열처리 조건하에서 비정질상은 미세한 $\alpha$-Fe 결정상의 석출 입자를 포함하는 혼합상으로 변태하는데 , 상기의 쵸크코어 특성은 주로 이들 미세 결정 입자에 의해 효과적으로 자벽 이동이 억제되고 자구가 미세화 되는 것에 기인하는 것으로 생각되었다.