Effect of $CaTiO_3$Additions on the Microwave Dielectric Properties of $Mg_2$$SiO_4$-$ZnAl_2$$O_4$Ceramics with Low Dielectric Constant

저유전율을 갖는 $Mg_2$$SiO_4$-$ZnAl_2$$O_4$계 세라믹스의 $CaTiO_3$첨가에 따른 고주파 유전특성

Effect of the microwave dielectric properties and the microstructure on a mole fraction(x=0.1~0.9) of (1-x)Mg$_2$SiO$_4$-xZnAl$_2$O$_4$ ceramics was investigated. When (1-x)Mg$_2$SiO$_4$-xZnAl$_2$O$_4$(x=0.1~0.9) ceramics were sintered at 130$0^{\circ}C$, 135$0^{\circ}C$ and 140$0^{\circ}C$ for 2hr, the microwave dielectric properties were obtained $\varepsilon$r=6.8~8.3, Q.f$_{0}$=36000~77600. On the other hand, the temperature coefficients of resonant frequency($\tau$$_{f}$) were obtained in the properties of -62ppm/$^{\circ}C$ to -49ppm/$^{\circ}C$. In order to adjust the temperature coefficient of resonant frequency($\tau$$_{f}$), CaTiO$_3$was added in (1-x)Mg$_2$SiO$_4$-xZnAl$_2$O$_4$ceramics. 0.7Mg$_2$SiO$_4$-0.2ZnAl$_2$O$_4$-0.1CaTiO$_3$ceramics sintered at 135$0^{\circ}C$ for 2hr showed the excellent microwave dielectric properties of $\varepsilon$r=7.7, Q.f$_{0}$=32000, and $\tau$$_{f}$=-7.9 ppm/$^{\circ}C$.EX>.>.EX>.