Abstract
NCZF ferrites doped with B-Bi-Zn(35-25-40) glass ceramics were prepared to investigate the magnetic properties. The XRD peaks of all of samples were observed only spinel phase. As the additive increased at sintering temperature 750$^{\circ}C$ and 850$^{\circ}C$ for 3 hours, the density and shrinkage of the samples increased until 5.28 g/cm$^3$ and 20% respectively. And other samples showed constant trends having the density about 5.4g/cm$^3$. According to SEM images the growth of grain progressed rapidly at sintering temperature of 850$^{\circ}C$ for 3 hours. Increasing the additive initial permeability and complex permeability decreased. The high values of complex permeability as a function of frequency showed that NCZF doped with 3 wt%, 5wt%, samples at sintered temperature of 850$^{\circ}C$/3h and 900$^{\circ}C$/3h.