Phase Transformation and Microstructural Change of Alumina Membrane

알루미나 여과막의 상전이와 미세구조 변화

  • Cheong, Hun (Department of Inorganic Materials Engineering, Han Yang University) ;
  • Choi, Duck-Kyun (Department of Inorganic Materials Engineering, Han Yang University) ;
  • Cheong, Deck-Soo (Multifunctional Ceramics Research Center, Korea Institute of Science and Technology)
  • 정훈 (한양대학교 무기재료공학과) ;
  • 최덕균 (한양대학교 무기재료공학과) ;
  • 정덕수 (한국과학기술연구원 복합기능세라믹연구센터)
  • Published : 2000.09.01

Abstract

Alumina membrane was prepared by sol-gel coating method using boehmite powder(${\Upsilon}-AlOOH$). The supported and the unsupported alumina membrane were fabricated to investigate the phase transformation and change of microstructure. It is important to control the homogeneous pore size and distribution in application of filtering process. The ${\theta}-to\;{\alpha}-AL_2O_3$ phase transformation (XRD) and the change of microstructure was investigated using scanning electron microscopy(SEM). XRD patterns showed that the supported membrane had $100^{\circ}C$ higher ${\theta}-to\;{\alpha}-AL_2O_3$ transformation temperature compared to the unsupported membrane. The similar effect was also observed for microstructural change of the membrane.

알루미나 여과막은 boehmite 분말 (${\Upsilon}-AlOOH$)을 이용하여 졸-겔법으로 준비되어졌다. 제조된 여과막은 상전이 온도와 미세구조 변화를 관찰하기 위해 지지체 없이 형성된 여과막을 제조하였다. 여과 공정의 응용에서 균일한 기공크기와 분포를 제어하는 것이 중용하다. 다공성 담체 위에 형성된 여과막과 다공성 담체 없이 형성된 여과막의 ${\theta}-to\;{\alpha}-AL_2O_3$로의 상전이는 박막 XRD를 이용하여 분석하였고, 미세구조의 변화의 관찰은 주사전자현미경(SEM)을 사용하여 관찰하였다. XRD에서 분석된 결과는 다공성 담체 위에 형성된 여과막이 다공성 담체 없이 형성된 여과막과 비교하여 $100^{\circ}C$ 더 높은 상전이 온도를 가지는 것을 보여주었다. 이런 유사한 효과는 여과막의 미세구조 변화에서도 관찰되었다.

Keywords

References

  1. Blackie Academic & Professional K. Scott;R. Hughes
  2. J. Am. Ceram. Soc. v.74 Y.S. Lin;A.J. Burggraaf
  3. Mater. Res. Soc. Symp. Proc. v.271 K.P. Kumar;V.T. Zaspalis;F.F.M. De Mul;K. Keizer;A.J. Burggraaf
  4. J. Am. Ceram. Soc. v.76 no.8 Q. Xu;Marc A. Anderson
  5. Ceram. Bull. v.70 no.4 K.K Chan;A.M. Brownstein
  6. J. Colloid and interface Sci. v.105 no.1 A.F.M. Leenaars;A.J. Burggraaf
  7. J. Am. Ceram. Soc. v.72 no.2 A.L. Larbot;J.P. Fabre;C. Guizard;L. Cot
  8. J. Membr. Sci. v.76 J.S. Gill;U.R. Marwah;B.M. Misra
  9. J. Membr. Sci. v.99 R.S.A. de Lange;J.H.A. Hekkink;K.Keizer;A. J. Burggraaf
  10. J. Am. Ceram. Soc. v.68 M. Kumagai;G.L. Messing
  11. J. Am. Ceram. Soc. v.81 no.8 I. Levin;D. Brandon
  12. J. Non-Crystalline Solids v.100 X. Yang; A. C. Pierre; D.R. Uhlmann
  13. J. Solids State Chem. v.30 S.J. Wilson
  14. J. Am. Ceram. Soc. v.65 no.9 F.W. Dynys;J.W. Halloran
  15. J. Mater. Sci. v.27 R.J.R Uhlhorn;M.H.B.J. Huis int Veld;K. Keizer;A.J. Burggraaf
  16. J. alloy and compounds v.290 H. Cheong;W.S. Cho;J.S. Ha;C.S. Kim;D.S. Cheong
  17. Powder Diffraction File, Card No. 11-0517 for θ-to α-Al₂O₃10-0173 for a-Al₂O₃
  18. J. Mater. Sci. v.27 J.H.L. Voncken;L. Lijzenga;K.P. Kumar;A.J. Burggraaf;B.C. Bonkamp
  19. Membrane Science and Technology Series v.4 A.J. Burggraaf;L. Cot
  20. Hemisphere Publishing Corporation (2nd. ed.) D.R. Gaskell
  21. Mater. Res. Soc. Symp. Proc. v.271 K.-N.P. Kumar;V.T. Zaspalis;F.F.M. Du Mul;K. Keizer;A.J. Burggraaf