Abstract
The effect of atmospheric annearling on the densification and electrical poperty of the Ca-doped $YCrO_3$were investigated. In order to study the densification and elecrical properties of $Y_{0.7}Ca_{0.3}CrO3$ the sample sintered at $1700^{\circ}C$ for 12hrs were subsequently annealed at $1400^{\circ}C$ under various atmospheres($O_2$, Air, $N_2$)as a function of time. The density of $Y_{0.7}Ca_{0.3}CrO3$ was $4.5/cm^3$ before annealing. Under the $N_2$ annealingm the bulk density of $Y_{0.7}Ca_{0.3}CrO3$ was increased to $4.9g/cm^3$ at 24hrs and then remained unchanged at 48hrs. When $Y_{0.7}Ca_{0.3}CrO3$nwas annealing at $1400^{\circ}C$ for 12hrs and 24hrs under $O_2$ activation energies were about 0.16eV at 12hrs and 24hrs, and showed 0.167eV below 400K, and 0.24eV over 400K at 48hrs.
열처리가 분위기 Y(sub)0.7Ca(sub)0.3CrO(sub)3<원문참조>의 치밀화 및 전기적 특서에 미치는 영향을 조사하였다. 1700$^{\circ}C$ 공기중에서 12시간 소결된 시편을 1400$^{\circ}C$ O$_2$, Air, N$_2$에서 시간의 변화에 따라 재열처리하였다. N$_2$분위기에서 열처리한 Y(sub)0.7Ca(sub)0.3CrO(sub)3<원문참조>의 밀도는 열처리 시간이 증가함에 따라 다음과 같이 변화하였다. 4.5(0hr)\longrightarrow5.35(24hrs)\longrightarrow5.1g/$cm^3$(48hrs). 전기전도도는 열처리 시간이 증가함에 따라 큰변화는 없었으며, 활성화 에너지는 0.16eV로 일정하였다. Air에서 재열처리한 경우 밀도는 거의 변하지 않았으나, 활성화 에너지는 시간에 따라 0.19에서 0.115eV까지 변화하였다. O$_2$분위기에서 열철한 Y(sub)0.7Ca(sub)0.3CrO(sub)3<원문참조>의 밀도는 24시간 열처리후 4.9(g/$cm^3$)로 증가후 일정하였다. 24시간 이상 N 분위기에서 열처리한 경우와는 다르게 기지상과 비슷한 조성의 제 2상의 석출되었으며 24시간동안 열처리한 시편까지는 전기 전도도에 변화가 없었다. 그러나 48시간 동안 열처리된 시편의 전기 전도도는 감소하였고 활성화 에너지는 400K이하에서 0.167eV, 400K 이상에서 0.24eV이었다.