Interpretation of Hydrothermal Synthesis of BaTiO3 Powder

BaTiO3 분말의 수열합성 해석

  • Oh, Jung Kang (School of Chemical Engineering & Biotech., Ajou University) ;
  • Seo, Kyung Won (School of Chemical Engineering & Biotech., Ajou University)
  • 오정강 (아주대학교 화학.생물공학부) ;
  • 서경원 (아주대학교 화학.생물공학부)
  • Received : 1998.11.24
  • Accepted : 1999.05.03
  • Published : 1999.06.10

Abstract

In Preparing $BaTiO_3$ powder under hydrothermal conditions, effects of reaction period feedstock concentration and mixing rate on crystallinity, mean size and size distribution of particles were studied. Experimental results showed that the particle size became smaller with its narrow distribution as the reaction period and mixing rate increased, but feedstock concentration decreased in contrast with the results based on the classical nucleation-growth model. From these results, $BaTiO_3$ particles seem to be prepared hydrothermally through a multiple reaction procedure that includes dissolution, precipitation, hydrolysis-condensation, aggregation, diffusion and transformation.

수열합성법을 이용한 $BaTiO_3$ 미세분말제조시 반응시간, 출발물질농도와 교반속도 등이 입자의 결정성, 평균입경과 입도분포에 미치는 영향을 조사하였다. 실험결과 기존의 핵생성-입자성장 모델과는 상이하게도 반응시간과 교반속도가 증가할수록 또는, 출발물질의 농도가 감소할수록 입자크기는 감소하였으며, 입도분포도 좁았다. 이로부터 $BaTiO_3$ 결정입자는 수열합성시 용해, 가수분해-축합반응, 침전, 응집, 확산, 전이 등의 복합적인 반응경로를 거치는 것으로 판단되었다.

Keywords

References

  1. J. Am. Ceram. Soc. v.64 M. Kuwabara
  2. IEEE Transmanuf. Tech. v.MFT-3 no.2 H. Ueoka;M. Yodogawa
  3. J. Mater. Sci. v.42 A. Meauger;J. C. Mutin;J. C. Miepce
  4. J. Eur. Ceram. Soc. v.8 D. Hennings;G. Rosenstein;H. Schreinemacher
  5. Kinetics of Precipitation A. E. Nielsen
  6. J. Am. Ceram. Soc. v.78 J. L. Look;C. F. Zukoski
  7. J. Am. Ceram. Soc. v.71 W. Herl
  8. J. Ceram, Soc. of Japan v.102 M Kondo;K Shnozaki;R. Ooki;N. Mizutami
  9. Crystallization(2nd ed.) Mullin, J. W
  10. Ferroelectrics v.28 N. G. Eror;T. M. Loehr;B. C. Cornilsen
  11. J. Am. Ceram. Soc. v.72 K. Uchnio;E. Sadanaga;T. Hirose
  12. 화학공학 PTC-BaTiO₃반도체 제조용 고순도 분말의 합성 오정강;서경원
  13. 화학공학의 이론과 응용 v.4 오정강;서경원
  14. Mater. Chem. Phys. v.19 T. R. N. Dutty;R. Vivekanandan;P. Murugaraj
  15. J. Am. Ceram. Soc. v.80 H. K. Park;D. K. Kim;C. H. Kim
  16. Chem. Mater. v.8 R. Asiaie;W. Zhu;S. A. Akbar;P. K Dutta
  17. J. Ceram. Soc. Japan v.102 M. Kondo;Z. Shinozaki;R. OlKi;N. Mizutani
  18. J. Am. Ceram. Soc. v.79 J. O. Eckert Jr;C. C. Hung;b. L. Gesten;M. M. Lenka;R. E. Riman