MICROLEAKAGE OF COMPOMER IN CLASS II CAVITY

제 2 급 와동에 충전된 Compome의 미세누출에 관한 연구

To evaluate the micro leakage of compomer, 4 materials were divided into 4 groups of 15 cavities each.(Group 1: Z-100, Group 2: Dyarct AP, Group 3: Fuji II LC, Group 4: Compoglass) After the class II cavities were prepared using carbide bur No. 553, all specimen were restored by incremental filling technique. In group 3, Z-100 was filled with a base of a light curing glass-ionomer. After 7 days, all specimens were thermocycled between $5^{\circ}C$ and $55^{\circ}C$ for 500 cycles, followed by placement in 50% silver nitrate dye for 2 hours at $37^{\circ}C$. After rinsed in distilled water, these teeth were immersed in photodeveloping solution and exposed to fluorescent light for 6 hours. Teeth were then washed in distilled water to remove the photodeveloping solution, sectioned mesio-distally and evaluated. The results were as follows : 1. In the cervical portion, there was significant difference between Fuji II LC and other groups(Z-100, Dyract AP, Compoglass), Fuji II LC had the least value.(p<0.05) 2. In the cervical portion, there was not significant difference among Dyract AP, Z-100 and Compoglass. 3. In the occlusal portion, there was not significant difference among Dyract AP, Z-100 and Compoglass. From the results above, In enamel, microleakage of compomer such as Dyract AP and Compoglass resemble to that of composite resin. It is thought that it is due to characteristics of composite resin portion of compomer. But in dentin, microleakage of compomer is higher than that of resin modified glass ionomer cement, it is thought that in compomer, acid-base reaction is not developed with dentin.