광중합형 복합레진 수리시 표면처리가 전단결합강도에 미치는 영향

THE EFFECT OF SURFACE TREATMENTS ON THE SHEAR BOND STRENGTH OF REPAIRED COMPOSITES

The purpose of this study was to evaluate the effect of surface treatments on the shear bond strength between new and old composites. Circular cavities prepared on the center of acrylic resin mold and the prepared cavities were filled with composite resin. They randomly assigned into control group and 8 groups according to the difference in surface treatments of old composites; Control group: no surface treatment, Group 1: surface treated with #120 SiC paper & bonding agent, Group 2: surface treated with #400 SiC paper & bonding agent, Group 3: surface treated with #120 SiC paper, 32% $H_3PO_4$ & bonding agent, Group 4: surface treated with #400 SiC paper, 32% $H_3PO_4$ & bonding agent, Group 5: surface treated with #120 SiC paper, primer & bonding agent, Group 6: surface treated with #400 SiC paper, primer & bonding agent, Group 7: surface treated with #120 SiC paper, 32% $H_3PO_4$, primer & bonding agent, Group 8: surface treated with #400 SiC paper, 32% $H_3PO_4$, primer & bonding agent. New composites were applicated on the old composites of experimental groups. The shear bond strengths for the experimental specimen were measured and the results were analyzed by using one way ANOVA. The observations of surface morphology after SiC paper roughening and debonded surface morphology after shear bond strength test were done by SEM. The results were as follows; 1. Shear bond strengths for specimens roughened with #120 SiC paper matching with the particle size of coarse diamond bur were significantly higher than those for the specimens with #400 SiC paper(P<0.05). By SEM, the surface of the specimens roughened with #120 SiC paper was more irregular than the specimens with #400 SiC paper. 2. Shear bond strengths for specimens treated with 32% $H_3PO_4$ etchant, primer, bonding resin were significantly higher than those for specimens treated with 32% $H_3PO_4$ and bonding resin(P<0.05). 3. Shear bond strengths for the specimens treated with 32% $H_3PO_4$ etchant and bonding resin were significantly higher than those for specimens treated with only bonding resin(P<0.05). There was no remarkable change of surface morphology after 32% $H_3PO_4$ etching. 4. It was possible to observe mixed fracture patterns (the cohesive fracture of old composite and the adhesive fracture between old and new composite) in the specimens roughened with #120 SiC paper, but almost adhesive fracture in the specimens roughened with #400 SiC paper.