EFFECT OF PHOSPHORIC ACID CONCENTRATION ON THE DIFFUSION OF HEMA THROUGH DENTIN

상아질을 통한 HEMA의 확산에 인산농도가 미치는 영향

The purpose of this study was to investigate the effect of phosphoric acid concentration on the movement of 2-hydroxyethylmethacrylate(HEMA) from bonding resin - resin composite combination through dentin in vitro. Freshly extracted human third molar teeth were divided into four groups each of 10 teeth. A closed chamber with 1 ml distilled water was attached to the CEJ of each tooth. An occlusal cavity of 4mm diameter & remaining dentin thickness of 1.0-1.5mm was prepared in each tooth. Dentin was treated with 10% phosphoric acid gel for 15 seconds. 32% phosphoric acid gel for 15 seconds, or with 35% phosphoric acid gel for 15 seconds. A control group not treated with acid gel was also prepared. The cavities were rinsed, dried and then treated with the HEMA-containing All-Bond 2 primer & bonding resin which was light-cured for 10 seconds. The cavities were then restored with Z100 composite resin(shade:A3.5:3M Dent. Prod. USA) & light cured for 30 seconds. Water samples were retrieved from the chambers over a time course (4.32, 14.4, 43.2, 144 & 432 minutes ; 1, 3 & 10 days) and analyzed by high performance liquid chromatography. The results were as follows. 1. HEMA was detected in the pulp chambers of all teeth from 4.32 minutes after resin placement The highest rate of release was in the first sample period (0-4.32 min) & rate of release declined exponentially thereafter. 2. No significant differences were found for mean release rate for HEMA over a time course among the four groups (p>0.05). 3. The diffusion rate was significantly (p<0.05) less for 10% phosphoric acid gel than 32% phosphoric acid gel at the second sample period(4.32-14.4 min). 4. No significant differences were found for cumulative HEMA diffusion among the four groups at 10 days(p>0.05) and mean total(cumulative) release at 10 days for all groups was in the 9 - 16 nmol range. 5. The cumulative release was significantly (p<0.05) less for 10% phosphoric acid gel than 32% phophoric acid gel at the third(14.4-43.2 min) & fourth(43.2-144 min) sample period.