Experimental Study on Properties of Permeable Polymer Concrete with Blast Furnace Slag and Fly Ash

고로 슬래그와 플라이 애시를 혼입(混入)한 투수성(透水性) 폴리머 콘크리트의 특성(特性)에 관(關)한 실험적(實驗的) 연구(硏究)

This study is performed to evaluate the properties of permeable polymer concrete with blast furnace slag and fly ash. The following conclusions are drawn: 1. The highest strength is achieved by 50% filled blast furnace slag powder and fly ash permeable polymer concrete, it is increased 36% by compressive strength and 217% by bending strength than that of the normal cement concrete, respectively. 2. The static modulus of elasticity is in the range of $100{\times}10^3{\sim}130{\times}10^3kgf/cm^2$, which is approximately 43~51% of that of the normal cement concrete. 3. The dynamic modulus of elasticity is in the range of $102{\times}10^3{\sim}130{\times}10^3kgf/cm^2$, which is approximately less compared to that of the normal cement concrete. The highest dynamic modulus is showed by 50% filled blast furnace slag powder and fly ash permeable polymer concrete. The dynamic modulus of elasticity are increased approximately 0~4% than that of the static modulus. 4. The water permeability is in the range of $4.612{\sim}5.913l/cm^2/h$, and it is largely dependent upon the mix design.

이 연구는 고로 슬래그 모래를 잔골재로 하여 고로 슬래그 미분말과 플라이 애시를 혼입한 투수성 폴리머 콘크리트의 특성을 구명한 것으로서, 이 연구를 통해 얻어진 결과를 요약하면 다음과 같다. 1. 강도는 고로 슬래그 미분말과 플라이 애시를 중량비로 50%씩 충전재로 사용한 투수성 폴리머 콘크리트에서 가장 크게 나타났고, 보통 시멘트 콘크리트보다 압축강도에서는 36%, 휨강동서는 207%가 증가되었다. 2. 정탄성계수는 $100{\times}10^3{\sim}130{\times}10^3kgf/cm^2$으로 보통 시멘트 콘크리트의 43~51%정도로서 변형성이 크게 나타났고, 충전재 배합별로는 고로슬래그 미분말과 플라이 애시를 중량비로 50%씩 사용한 투수성 폴리머 큰크리트에서 가장 큰 값을 보였다. 3. 동탄성계수는 $102{\times}10^3{\sim}130{\times}10^3kgf/cm^2$로서 보통 시멘트 콘크리트보다 작게 나타났고, 고로슬래그 미분말과 플라이 애시를 50%씩 충전재로 사용한 투수성 폴리머 콘크리트에서 가장 큰 값을 보였으며, 동탄성계수는 정탄성계수보다 약 0~4%정도 큰 값을 보였다. 4. 투수량은 $4.612{\sim}5.913l/cm^2/h$로서 배합설계에 따라 크게 좌우되었으며, 이러한 콘크리트는 투수를 요하는 구조물에 유용하게 이용할 수 있을 것이다.