A Study on the Enhanced Cleanup of Mine Tailings Using Thiobacillus ferrooxidans

Thiobacillus ferrooxidans를 이용한 광미 정화의 효율 증진에 관한 연구

This study was carried out to enhance the efficiency of bioleaching of heavy metals. copper and zinc from the soil samples obtained from mine tailings in Cho-il Mine located in Dan-Yang, Choong-Buk. The effects of medium (9 K) composition on the leaching efficiency were investigated by changing concentrations of the dominant components. phosphorus, nitrogen source. and energy source which are the most important factors governing the growth and multiplication of microorganism. The results of the bioleaching test at different phosphorus concentrations of medium, 0 mM. 3.0 mM, and 6.0 mM showed that leaching efficiency for zinc and copper was 98.8% and 47.5% respectively at 0 mM and decreased at higher phosphorus concentration 6.0 mM. In the bioleaching test of zinc and copper at 0 mM, 45 mM, and 90 mM nitrogen concentrations, the Highest efficiency of 85% and 46.4% was obtained for zinc and cooper respectively at 45 mM and the lower efficiency observed for 90mM nitrogen addition. The zinc and copper leaching with variation of energy source dosage showed the highest removal efficiency, 93% for zinc in the absence of energy source and 46.4% for copper at 160mM energy source.

충북 단양에 위치한 조일 광산에서 채취한 구리와 아연으로 오염된 광미(광산 폐기물로서 금속 추출 후 남은 찌꺼기) 처리방안으로서 생물학적 용출기법(bioleaching)의 효율 증진에 관한 연구를 수행하였다. 기본 배지 조성(9 K medium) 중 미생물의 성장 및 증식에 영향을 미치는 에너지원, 인, 질소원의 농도를 변화시켜가며 배지 조성에 따른 중금속의 생물학적 용출 특성을 관찰하였다. 먼지, 배지조성 중 인의 농도를 0 mM. 3.0 mM, 6.0 mM 각각 조절하여 중금속의 용출효율을 관찰한 결과. 인을 첨가하지 않았을 때 아연. 구리 각각 98.8%와 47.5%의 용출효율을 보인 반면 인의 농도가 6.0mM 로증가 시켰을 경우. 오히려 중금속의 용출효율이 감소하였다. 배지내 질소원의 농도를 0 mM. 45 mM, 90 mM로 조절하여 중금속의 용출정도를 알아본 결과. 45 mM 농도로 주입하였을 때 아연. 구리 각각 85%,와46.4%로 90 mM 농도에보다 더 높은 용출효율 나타내었다. 에너지원 변화에서는 아연의 경우 에너지원을 첨가하지 않았을 때 93%의 용출효율을 보였고. 구리의 경우는 160 mM 첨가했을 때 46.4%로 가장 높은 중금속 용출효율을 보였다.