Compressive Strength Reduction Characteristics of Linerboard as Influenced by Temperature and Humidity

온도 및 습도 변화에 따른 라이너원지의 압축강도 열화에 관한 연구

Compressive strength reduction characteristics of 4 different linerboards(SC, KA, SK and IK) as influenced by temperature and humidity were investigated by ring crush test. No significant effect of temperature on the reduction of compressive strength was found for samples prepared at 5$^{\circ}C$ and 30$^{\circ}C$. At the relative humidity of 66 percents, IK linerboard showed the lowest reduction of the compressive strength. At the relative humidity of 93 percents, KA linerboard lost 40 percents of its initial compressive strength while SK linerboard lost its strength up to 56 percents. The result indicated that KA linerboard was the most cost effective and material with the highest compressive strength among tested linerboards.

온도 및 습도 변화에 따른 라이너원지의 압축강도 열화를 측정한 결과 압축강도는 온도변화에 영향이 없는 것으로 나타났다. 습도변화의 경우 66% RH에서는 IK원지의 강도저하가 가장 낮은 것으로 나타났다. 93% RH에서는 KA원지의 강도저하가 40%로 가장 낮았으며 SK원지가 56%로 가장 높게 나타났다. 비압축강도의 경우 66% RH에서는 SC 마니라와 IK 원지가, 93% RH에서는 IK원지와 KA원지가 가장 우수하였다. 원 단위 압축강도에서는 습도를 무시할 경우 SK원지가 우수하였으나 66% RH와 93% RH에서는 모두 KA원지가 다른 원지보다 우수한 것으로 나타났다. 따라서 농산물 포장용 라이너로 KA원지를 사용할 경우 경제적이면서도 압축강도가 높은 골판지상자를 제조할 수 있을 것으로 판단된다.