Abstract
Diamond-like carbon(DLC) films were synthesized using the rf-plasma CVD technique with the addition of small amounts of nitrogen and oxygen to a gas mixture of $CH_4$ and $H_2$. The gas flow ratio of $CH_4$ to $H_2$ was 2.4:1, and 3% , 13.6% of nitrogen were added to the gas mixture of $CH_4$ and $H_2$ for the deposition of DLC films. The film stress tended to decrease as the nitrogen concentration increased from 3% to 13.6%, probably due to the decrease of the number of the interlink between carbon atoms. The residual stress tended to slightly decrease when 3% of oxygen was added. Scratch tests were performed to investigate the adhesion between the DLC films and the Ti intelayer after pretreating the TiN surface with direct hydrogen plasma. The adhesion was enhanced by adding nitrogen and oxygen to the $CH_4$ and $H_2$ gas mixture. The adhesion for the 3% nitrogen addition was better than that for the 13.6% nitrogen addition. The Vicker's hardness of the DLC films was measured to be 1100Hv.