급속응고법으로 제작한 Zr기 수소저장합금의 전극특성

The Electrode Characteristics of the Zr-based Hydrogen Absorbing Alloy Fabricated by the Rapid Solidification Process

  • 발행 : 1999.04.01

초록

The charge-discharge, the high-rate dischargeability, and the self discharge characteristics of the electrodes composed of rapidly solidified ZrV\ulcornerMn\ulcornerMo\ulcornerNi\ulcorneralloy, which has the form of partial substitution of Mn, Mo, Ni for V in $ZrV_2$ were studied. The alloys were prepared using Arc & RSP(Rapid Solidification Process) at the rotating roller speed of 2000 and 5000 rpm. Some of them were received heat treatment at$ 560 ^{\circ}C$ for 1 hour after the solidification to investigate the effect of the heat treatment. It was fond that cycle life was significantly improved by RSP, whereas discharge capacity, activation rte and high rate dischargeability were decreased compared with the conventional arc melting method. The capacity loss seems to be due to the loss of the crystallinity and the increase of the cycle life ascribed to the presence of the amporphous phase as well as the refined grain size of less than 0.2$\mu\textrm{m}$. Heat treatment of the alloy cooled at 2000 rpm improved the cycle life. In case of the alloys cooled at 5000 rpm, both the discharge capacity and the activation rate were significantly improved by the heat treatment.

키워드

참고문헌

  1. Met. Trans. JIM v.31 no.487 H. Sawa;S. Wakao
  2. J. Less-Common Met. v.104 no.365 S. Wakao;U. Uomemura;H. Nakano;H. Shimada
  3. fur Phys. Chem. Neue Folge v.164 no.1515 C. Poinsignon;M. Forestier;Zeit
  4. J. Less-Common Met. v.172 no.1219 S. Wakao;H. Sawa;J. Furukawa
  5. DENKI KAGAKO v.59 no.11 S. Wakao;H. Sawa
  6. J. Alloys and Comp. v.192 M. Matsuoka;K. Asai;Y. Fukumoto;C. Iwakura
  7. Electrochimica Acta v.27 no.12 T. Kitamura;C. Iwakura;H. Tamura
  8. Electrochemical Society Proceedings v.92 no.5 B.K. Zoitos;D.L. Hudson;P.D. Bennet;V.J. Puglisi
  9. Electrochimica Acta v.40 no.5 C. Iwakura;I. Kim;N. Matsui;H. Inoue;M. Matsuoka
  10. J. Electochem. Soc. v.140 no.3 M. Ciureanu;D.H. Ryan;J.O. Strom-Olsen;M.L. Thrudeau
  11. J. Electochem. Soc. v.141 no.12 M. Ciureanu;J.O. Strom-Olsen;D.H. Ryan;P. Rudkowski;G. Rudkowska;B. Bondoc
  12. J. Alloys and Comp. v.231 no.321 L.K. Varga;A. Lovas;K. Tompa;M. Latroche;A. Percheron-Guegan
  13. Electrochimica Acta v.43 no.1839 C. Li;X. Wang;X. Li;C. Wang
  14. J. Alloys and Comp. v.180 no.37 T. Sakai;H. Yoshinaga;H. Miyamura;N. Kuriyama;H. Ishikawa
  15. J. the Korean Hydrogen Energy Society v.8 no.3 정치규;한동수;정원섭;김인곤;김원백
  16. J. Alloys and Comp. v.192 no.152 C. Iwakura;Y. Fukumoto;M. Matsuoka;T. Kohno;K. Shinmou