A Study on the Preparation of Wood-Polymer Composites with Recycled PE films

재활용 PE수지를 이용한 Wood-Polymer Composites 제조에 관한 연구

  • Kim, Ryeun-Kwan (Department of Materials Science & Engineering, and Energy & Environmental Research Center Kwangju Institute of Science & Technology (K-JIST)) ;
  • Kang, Min (Department of Materials Science & Engineering, and Energy & Environmental Research Center Kwangju Institute of Science & Technology (K-JIST)) ;
  • Kim, Hea-Tae (Korea Resources Recovery & Reutilization Corporation) ;
  • Song, Byung-Sun (Korea Resources Recovery & Reutilization Corporation) ;
  • Yoon, Tae-Ho (Department of Materials Science & Engineering, and Energy & Environmental Research Center Kwangju Institute of Science & Technology (K-JIST))
  • 김륜관 (광주과학기술원 신소재공학과/에너지환경연구센타) ;
  • 강민 (광주과학기술원 신소재공학과/에너지환경연구센타) ;
  • 김혜태 (한국자원재생공사) ;
  • 송병선 (한국자원재생공사) ;
  • 윤태호 (광주과학기술원 신소재공학과/에너지환경연구센타)
  • Published : 1999.10.01
Download PDF
⟨ Previous Next ⟩

Abstract

Wood-Polymer Composites (WPC) m s prepared irom recycled films of agricullural use and wood wastes, and LLDPE and neal PE resin mlxlurr war also utilized in order to cornpiue the praperlies. Molc~ca nhydride (MA) and dicumyl peroxide were used as an adheslon pmmoler and an il~lliatotor~, .espcmivelyT. ensile prapenies of W Cw zrc measured via lenslle test as a funclieu of woad lille~m d MA contmt, and rractu1.e surface was also mvestigaled wilh SEM. As the content of wwd tiller mcreased, clongauon deneased bul modulus increased However, tensile slrength OI WPC increased only when MA war used, and 1 wt.% of MA may be hgh enough to increase the tensile properties. The tensilc ptopcrlies af WPC prepwed from recycled PE films were &nost same as thosc of neal PE resin mixture.

재활용된 농업용 폐비닐과 목재부산물로부터 Wood-Polymer Composites (WPC)을 만들었으며, 또한 LLDPE 및 혼합 polyethylene으로 만들어진 WPC와 비교하였다. 접착성 향상제로 maleic anhydride를 사용하였으며, 이의 개시제로 dicumyl peroixde를 첨가하였다. 접착성 향상제로 maleic anhydride를 사용하였으며, 이의 개시제로 dicumyl peroixde를 첨가하였다. 제조된 WPC의 물성은 인장강도 시험으로 측정하였으며, 목재 및 접착성 향상제의 첨가량에 따라 분석하였다. 또한 파단면을 SEM을 이용하여 분석하였다. 목재의 양이 증가함에 따라 WPC의 신율은 감소하고, 탄성율은 증가하였다. 하지만 인장강도는 MA가 첨가된 경우에만 증가하였으며, MA 1% 첨가로 크게 증가하였지만 더 이상의 첨가는 효과가 없었다. 농업용 재활용 비닐로 제조된 WPC의 물성은 구매된 PE 수지로 제조된 WPC와 비슷한 값을 보였다.