A Study on the Properties of Alumina Ceramics as the Amount of $\textrm{TiO}_2$ Addition

$\textrm{TiO}_2$ 첨가량에 대한 알루미나 세라믹스의 특성에 관한 연구

The effects of Tio$_2$addition on the microstructural evolution and mechanical properties of alumina ceramics were studied. Bulk density decreased with an increase of the amount of TiO$_2$. Apparent porosity decreased with an increase of the amount of TiO$_2$ up to 7wt%. But beyond 9wt% of TiO$_2$powders, apparent porosity increased. In the compression test, the modulus increased with an increase of the amount of TiO$_2$addition. In the three point bending test, the stress at yield decreased with an increase of the amount of TiO$_2$ addition. The addition. The addition of TiO$_2$ promoted the grain growth of alumina ceramics.

TiO$_2$분말을 $Al_2$O$_3$분말에 대하여 무게비로 1,3,5,7,9와 11wt%로 혼합하여 알루미나 세라믹스의 미세조직 및 기계적 물성변화를 관찰하였다. TiO$_2$분말의 첨가량이 증가할수록 부피비중은 3.26에서 2.90g/㎤으로 감소하였으며 기공율은 TiO$_2$분말의 첨가량이 7wt%까지는 감소하였으나 9wt%이상 첨가할 경우 증가하였다. 압축강도 측정 결과 파괴강도는 TiO$_2$분말의 첨가량이 7wt%까지는 증가하였으나 9wt%이상 첨가할 경우 감소하였다. 3점 곡강도를 측정한 결과 최대 파괴 응력 값은 TiO$_2$분말의 첨가량이 증가할수록 감소하였다.