Abstract
Si3N4 -Si3N4 joints were made using Ag-Cu-Ti and Ag-Cu-In-Ti via brazing method and the change in joint strength was investigated after heat treatment at $400^{\circ}C$ or $650^{\circ}C$ for up to 2000h. The initial strength of as-brazed joints with Ag-Cu-In-Ti was lower but the reduction of the strength was less dramatic than that with Ag-Cu-Ti. The joints made of a new brazing alloy Au-Ni-Cr-Mo-Fe which is developed for high temperature applications were heat-treated at $650^{\circ}C$ for 1000h. As the heat treatment time increased the bond strength increased. The results of the joining system with Mo or Cu interlayer showed that the strength of the joint with Mo interlayer was higher but the system incurred problems in joint production Also it was found from oxidation experiment that Ti and In affected the oxidation resistance of brazing alloy.
본 연구에서는 Ag-Cu-Ti 와 Ag-Cu-In-Ti 를 사용하여 브레이징법으로 질화규소 간 접합체를 제작하고 $400^{\circ}C$와 $650^{\circ}C$에서 장시간(2000 h) 열처리 후 파괴 강도의 변화를 살펴보았다. 접합후 강도는 Ag-Cu-Ti 가 높게 나왔지만, 열처리 시간이 증가할수록 Ag-Cu-In-Ti 의 경우가 강도의 감소 정도가 작은 것으로 나타났다. 또한 고온 응용을 위해 개발된 새로운 접학 합금인 Au-Ni-Cr-Mo-Fe 계를 이용하여 질화 규소 간의 접합체를 제작하여 $650^{\circ}C$에서 100시간까지 장시간 열처리 하였다 접합 당시의 강도는 상용 접합 합금보다는 낮은 값을 보였지만, 열처리를 함에 따라 강도의 증가를 보였다 SUS316과의 접합시에는 중간재로 몰리브데늄 또는 구리를 사용하였으며 $400^{\circ}C$에서 1000시간 동안 열처리하였다. 강도는 몰리브데늄을 사용한 경우가 높게 나왔지만, 접합체의 형성이 어렵다는 단점이 있었다. 산화 실험에서는 Ti가 첨가된 접합 합금인 Ag-Cu-Ti 의 경우가 첨가되지 않은 Ag-Cu의 경우보다 산화가 잘 일어나며, 인듐을 첨가한 Ag-Cu-In-Ti 의 경우는 산화 억제의 효과가 나타났다. 전반적으로 In을 포함한 접합 합금이 고온 신뢰도 면에서 우수한 것으로 나타났다.