Abstract
For dolomite clinkers used as stamp materials, the corrostion behavior of those by slag was inverstigated between 1550$^{\circ}C$ and 1650$^{\circ}C$. Fe2O3 among slag components was selectively penetrated into the grain boundaries of dolomite clinkers. In hot face, the magnesioferrite was preferentially formed by Fe2O3 component contained in dolomite clinker rather than Fe2O3 of slag. The corrosion steps of dolomite clinkers by slag were found as follows ; (1) The dicalciumferrite was formed by the reaction of the calcia within dolomite clinkers with Fe2O3 of slag. (2) The magnesia within dolomite clinkers reacted with the dicalciumferrite to from magnesioferrite and the residual calcia within dolomite clinkers reacted with the dicalciumferrite to form magnesioferrite and the residual calcia was dissolved into slag. (3) The magnesioferrite was corroded by CaO-SiO2 compounds of slag. With the temperature of slag increased, the magnesioferrite layer in hot face was decreased for dolomite clinker without Fe2O3 while the layer thickness and grain sizes of magnesioferrite was increased for dolomite clinker with Fe2O3.
155$0^{\circ}C$~1$650^{\circ}C$의 온도범위에서 stampwo의 원료로서 사용되는 돌로마이트 클링커의 Fe2O3의 함유유무에 따른 slag에 의한 침식거동을 연구하였다. Slag 성분중에서 CaO-SiO2계 저융점 화합물 보다는 Fe2O3가 선택적으로 돌로마이트 클링커의 입계로 깊숙히 침투되었다. 돌로마이트 클링커의 가동면에 존재하는 치밀한 magnesioferrite는 slag중의 Fe2O3 성분보다는 클링커중에 함유되어 있는 Fe2O3 성분에 의하여 우선적으로 생성되었다. 돌로마이트 클링커의 slag에 의한 손상은 돌로마이트 클링커의 입계에 존재하는 CaO가 slag중의 Fe2O3 성분과 반응하여 dicaciumferrite를 생성$\longrightarrow$dicalciumferrite가 slag 성분중의 CaO-SiO2계 화합물에 의하여 용출되는 단계로 진행되었다. Slag의 온도가 상승됨에 따라 Fe2O3가 함유되어 있지 않는 돌로마이트 클링커의 경우에는 돌로마이트 클링커의 가동면에 생성되는 magnesioferrite의 층은 미양하였다. 반면에, Fe2O3가 함유된 돌로마이트 클링커는 slag의 온도가 상승됨에 따라 magnesioferrite의 층이 두꺼울 뿐문아니라 magnesioferrite의 입성장도 수반되었다.