WC-Co Milling Inserts Manufactured by Powder Injection Molding

분말사출성형에 의한 WC-Co 계 milling insert 제조

  • 성환진 (포항산업과학연구원 소재연구부문)
  • Published : 1999.03.01

Abstract

The purpose of this study is to investigate the manufacturing feasibility of WC-Co milling inserts via Powder Injection Molding (PIM) process. WC-Co is used in a wide variety of cutting tools due to its high hardness, stiffness, compressive strength and wear resistance properties. WC-Co parts for a high stress application were conventionally produced by the press and sinter method, which were Iimited to 2 dimensional shapes. Manufacturing WC-Co parts for a high stress application by PIM implies that tool efficiency can be highly improved due to increased freedom is design. P30 grade WC powder (WC-Co-TiC-TaC system) was mixed with RIST-5B133 binder and injection molded into milling inserts (Taegu Tech. Model WCMX 06T 308). The mean grain size of the powder was about 0.8$\mu$m. Injection molded specimens were debound by solvent extraction and thermal degradation method at various conditions. The specimens were sintered at 140$0^{\circ}C$ for 1 hr in vacuum. Carbon content, weight loss, dimensional change, and macro defects of the specimen were carefully monitored at each stage of the PIM process. PIMed WC-Co milling inserts reached 100% full density after sinteing. Its mechanical properties and micro-structures were comparable with the press and sintered milling insert. Carbon content of the sintered WC-Co insert was mainly determained by the atmosphere of thermal debinding. By controlling powder loading and injection molding condition, dimensional accuracy could be obtained within 0.4%. We confirm that PIM can not only be an alternative manufacturing method for WC-Co parts economically but also provide a design freedom for more effieient cutting tools.

Keywords

References

  1. Int. J. Refractory Metals and Hard Meterials v.12 M. T. Martyn;P. J. James
  2. Proc. of the World Congress on High Tech Ceramics S. Uram;Milan(Ed.);P. Vincenzini(Ed.)
  3. MPIE R. M. German
  4. Advanced in Powder Metallurgy & Particulate Materials-1994 v.4 M. Yang;R. M. German
  5. J. Jpn. Soc. Powder Powder Metall. v.44 H. Miura;Y. Sakajiri;M. Okada;K. Takari
  6. 1st Japan-Korea Workshop on Powder Injection Molding-Cheju A. Matruo;S. Sakaguchi;T. Hirayama;S. Ahn(Eds.);Nack J. Kim(Eds.)
  7. Advanced in Powder Metallurgy & Particulate Materials-1995 v.13 M. Yang;R. M. German
  8. 超硬合金と燒結硬質材料(基礎と應用) 鈴木壽(編著)
  9. 日本金屬學會誌 v.11 鈴木壽
  10. Planseeber. Pulvermet. v.14 H. Suzuki;H. Kubota
  11. 日本金屬學會誌 v.31 鈴木壽(et al.)