The Preparation of a Polyimide Membrane for the Separation of Water-Acetic Acid Mixture through Pervaporation

Polyimide 막에 의한 물-초산계의 투과증발 분리

  • 박영태 (경일대학교 공과대학 화학공학과)
  • Published : 1999.12.01

Abstract

The asymmetric polyimide [PI] membrane with good solvent-resisting and heat-resisting properties was prepared by using the phase inversion method from polyamic acid, and its pervaporation separation characteristics of water-acetic acid system were studied. It was appeared from the prepared membranes that the best non-solvent of polyamie acid for the phase inversion was toluene. The best heat-treatment condition for the imidization of polyamic acid was 1 hr heating at each of the temperatures, 373, 473, and 573 K The thermal durability and chemical stability during the pervaporation separation of water-acetic acid of the prepared PI membrane was superior. The pervaporation characteristics of prepared membrane were 180 of separation factor and 0.5 kg/$m^2$hr of total flux for 80 wt% acetic acid feed.

고농도의 초산수용액(80 wt% 이상)을 분리 농축하기 위하여 내용매성이 우수하며 고온에서의 내열성을 가지는 폴리이미드 비대칭막을 만들어 막의 특성을 검토하고 물-초산 계의 투과증발 분리성능을 고찰하였다. 제막은 폴리아믹산의 상전이용액으로 톨루엔을 사용한 것이 가장 좋은 상태의 막을 얻을수 있었다. 열처리에 의한 imide화는 373, 473573 K에서 각각 1시간씩 연속적으로 처리하는 것이 가장 효과적이었다 막은 물-초산 계의 투과증발 분리에 의한 열내구성 및 화학적 안정성이 우수하였다 폴리이미드막의 투과증발 분리특성은 80 wt% 초산수용액 계에서 분리계수는 180 투과유속은 0.5kg/$m^2$hr을 얻을 수 있었다.

Keywords

References

  1. I&EC v.53 R.C. Binning;R. J. Lee;J. F. Jennings;E. C. Martin
  2. I&EC Fundtls. v.4 B. B. Long
  3. Memb. & Memb. Processes H. E. A. Bruschke;G. F. Tusel
  4. 膜(Maku) v.10 M. Yoshikawa;T. Takahashi;K. Sanui;N. Ogata
  5. J. Memb. Sci. v.43 R. Y. M. Huang;Y. F. Xu
  6. 멤브레인 v.6 임지원;염충균;김선우
  7. Membrane Symposium(Japan) v.5 岡本健一;谷原望;田中一宏;喜多英敏
  8. Chem. Lett. v.12 H. Kita;S. Sasaki;K. Tanaka;K. Okamoto;M. Yamamoto
  9. Polymer J. v.17 M. Yoshikawa;H. Yokoi;K. Sanui;N. Ogata
  10. J. Memb. Sci. v.11 A. Iwama;Y. Kazuse
  11. Kobunshi Ronbunshi v.49 H. Yanagishita;K. Nakane;H. Yoshitome
  12. 膜(Maku) v.15 H. Ohya;H. Futamura;T. Ichihara;Y. Negishi;K. Matsumoto
  13. U.S. Pat. Appl. v.316 W.J. Wrasidlo
  14. U.S. Appl. v.273 C.W. Alegranti
  15. 公開慝許 57-170 宇部興産
  16. 公開特許 57-170 宇部興産
  17. 公開特許 57-170 宇部興産