Quantitative Evaluation of Fatigue Strength by Spheroidal of Graphite in Ductile Cast Iron

구상화율에 의한 구상 흑연주철재의 피로강도의 정량적 평가

  • Published : 1999.10.01

Abstract

Although the problems of defects and nonmetallic inclusion in metal fatigue are very complicated it is particularly important to view these problems from the perspective that defects and inclusions are virtually equivalent to small cracks. This concept will help us to understand various fatigue phenomena caused by graphite of Ductile cast iron. Therefore in this study different ferrite-pearlite matrix structure and pheroidal ratio of graphite of 70%, 80% and 90% GCD40 , GCD45-2 series have been carried out rotary bending fatigue test estimated the maxi-mum size of graphite investigated correlation. It was concluded as follows : (1) in ductile cast iron which have various spheroidal ratio of graphite the fatigue limit C series of 90% spheroidal ratio of graphite is the highest. While A series of 70% spheroidal ratio of graphite is the lowest (2) fatigue limit was predicted by vickers hardness(Hv) of matrix {{{{ SQRT {area } }}}} of maximum size graphite inputting Murakami and Endo's formula.

Keywords

References

  1. Miller and Company The Duc-tile Process A.F.Spengler(ed.);H.K. Briggs(ed.)
  2. Ductile Iron Ⅰ Stephen I. Karsay
  3. Ductile Iron Ⅲ Stephen I. Karsay
  4. 日本機械學會論文集 v.60 no.570 球狀黑鉛鑄鐵の疲勞破面解析と黑鉛の擧動 土居滋
  5. 한국공작기계학회지 v.7 no.5 구상흑연 주철재의 피로크랙 발생 및 피로강동에 미치는 기지조직의 영향 尹命辰;李慶模
  6. ASME v.109 Effects of an Artificial Small defect ofn Torsional Fatigue Strength of Steels Masashiro Endo;Yukitaka Murakami
  7. Fatigue v.16 Effects of Defects, inclusions and inhomogeneities on Fatigue Strength Yukiaka Murakami;M. Endo
  8. JSME v.32 no.2 effects of Small Defects and Nonmetallic Inclusions on The Fatigue Strength of Metals Yukitaka Murakami
  9. J. Res. Natl. Inst. Stand. Technol. v.99 Inclusion Rating by Statistics of Extreme Values and Its Application to Fatigue Strength Prediction and Quality Control of Matcri-als Y. Muraksmi
  10. EFM v.17 no.3-A Growth and Sta-bility Of Interacting Surface Flaws of Arbitrary Shape Y. Murakami;S. Nemat-Nasser
  11. The Behaviour of Short Fatigue Cracks Effects of Hardness and Crack Geometries on ${\Delta}\;{K_th}$of Small Cracks Ema-nating from Small Defects Murakami Y.;Endo M.;K. J. Miller(ed.);E.R. de los Rios(ed.)
  12. 日本機械學會論文集 v.54 no.499 疲勞强度に及ばす介在物, 微小缺陷, 微小き裂の影響 村上敬宣;淸水眞佐男
  13. 日本機械學會論文集 v.50 no.457 回轉曲げを受ける球狀黑鉛鑄鐵の微小き裂發生および進展擧動 加藤容三;中野典彦
  14. 材料 v.43 no.493 最近の球狀黑鉛鑄鐵の疲勞强度におよばす黑鉛と人工微小缺陷の影響 遠藤正浩;王羽兵
  15. 日本機械學會論文集 v.58 no.556 球狀黑鉛鑄鐵切缺材の疲勞强度 西谷弘信(外3人)
  16. 材料 v.42 no.481 各種人工微小缺陷および微小缺陷の相互干涉效果が疲勞限度におよばす影響 鳥山壽之;村上敬宣