Repassivation Characteristics of Fe-Cr Steels Using the Abrading Electrode Technique in Aqueous 0.1M $Na_2SO_4+ NaCl$ Solutions

0.1M $Na_2SO_4+ NaCl$ 수용액에서 마멸 전극 기법을 이용한 Fe-Cr강의 재부동태 특성

  • Ham Dong Ho (School of Metallurgical and Materials Engineering, Kookmin University) ;
  • Lee Jae Bong (School of Metallurgical and Materials Engineering, Kookmin University)
  • 함동호 (국민대학교 공과대학 금속재료공학과) ;
  • 이재봉 (국민대학교 공과대학 금속재료공학과)
  • Published : 1999.11.01
Download PDF
⟨ Previous Next ⟩

Abstract

The repassivation characteristics of Fe-Cr steels in deaerated 0.1 M $Na_2SO_4$ solution have been investigated with the variation of Cr content, applied potential and Cl- concentration. In the absence of chloride ion, abrading electrode test showed that, slope -n, of log i=k -n log t, a parameter of repassivation rate, approached to -1, regardless of Cr content but as Cr content increased, repassivation current density decreases with increasing Cr content. A.C. Impedance spectroscopy showed that the charge transfer resistance of passive film became higher as Cr content and applied potential increased. However, in the presence of chloride ion, it was observed that chloride ion suppressed the passive film formation, whose effect became greater with increasing applied potential.

탈기된 0.1 M $Na_2SO_4$ 수용액에서 Fe-Cr강의 재부동태 특성을 Cr함량, 인가전위 그리고 염소이온의 농도를 변화시키면서 관찰하였다. 염소이온이 없는 경우 재부동태 속도를 나타내는 식 log i=k-n log t에서 -n값은 Cr함량에 관계없이 -1에 수렴하였으나 Cr함량이 증가할수록 재부동태 전류밀도는 낮아졌다. A. C. impedance spectroscopy측정 결과, Cr 함량과 인가전위가 증가할수록 형성된 재부동태 피막의 charge transfer resistance$(R_{ct})$ 값은 상승하였다. 또한 재부동태 동안 흐르는 전류밀도를 Faraday식을 이용하여 피막의 두께를 계산해보면 Cr함량이 증가할수록 얇은 부동태 피막이 형성된다는 것을 알 수 있었다. 그러나 염소이온이 존재하는 경우, 염소이온이 Fe-Cr강의 재부동태를 방해하는 효과는 인가전위가 증가할수록 상승하였다.