A Study on the Fabrication of Lithium Iron Oxide Electrode and its Cyclic Voltammetric Characteristics

리튬-철 산화물 전극의 제조 및 전류전위 순환 특성에 관한 연구

Various types of iron oxide based materials as a cathode of lithium secondary battery have been prepared and their electrochemical characteristics have been also observed. In order to understand the fundamental characteristics of iron oxide electrode, three kinds of iron oxides such as iron oxides formed by direct oxidation of iron plate or iron powders and FeOOH powders were tested with cyclic voltammetry. The oxidation and reduction peaks due to the reaction of intercalation and deintercalation were not observed for the iron oxide prepared with iron plate and FeOOH powders. In case of iron oxide prepared from iron powders, only one reduction peak was observed. A layered form of $LiFeO_2$ was synthesized directly from $FeCl_3\cdot6H_2O,\;NaOH\;and\;LiOH$ and LiOH by hydrothermal reaction. The effect of NaOH on the electrode performance was examined. When increasing NaOH, it provides the electrode with less discharge capacity and efficiency, however, decreasing rate of discharge capacity became smaller. $LiFeO_2$ synthesized with the molar ratio of $NaOH/FeCl_3/LiOH$, 2/1/7 showed the largest capacity, but the discharging efficiency was sharply decreased after 30 cycles.

본 연구에서는 리튬전지 내 양극 재료로서 리튬-철계 산화물의 응용가능성을 모색하기 위하여 여러 제조방법에 따라 변화되는 전기화학적 특성을 고찰하고자 하였다. 철산화물에 대한 기본적인 양극 전기화학적 특성을 관찰하기 위해 철판, 철분말을 산화시켜 제작한 전극과 FeOOH 분말로 제작한 전극을 전류전위 순환실험을 실행하였다. 그 결과 철판과 FeOOH분말 전극의 경우 거의 리튬 층간의 산화-환원 반응이 일어나지 않음을 알 수 있었으며 철 분말의 산화물 전극에서는 리튬이온의 환원반응 피크는 보이나 산화반응은 거의 관찰되지 않았다. 또한 출발 물질 $FeCl_3-6H_2O,\;NaOH.\;LiOH$를 혼합하여 저온으로 가열하여 층상의 $LiFeO_2$를 합성하였으며, 출발 물질의 조성비를 바꾸어 그 영향을 조사하였다. 그 결과 NaOH의 첨가량이 증가할수록 전극의 용량과 효율은 감소하나 용량의 감소율은 작아짐을 알 수 있었다. $NaOH/FeCl_3/LiOH$의 몰 비를 2/1/7로 조성하여 합성하였을 때 가장 큰 용량을 보였으나 효율은 30회 순환 후 급격히 감소하였다.