Behaviour of the Fretting Wear and Corrosion Characteristics on a Hinge Material

힌지재료의 부식특성 및 찰과마멸 거동

  • Kwak Nam-In (Dept. of Die & Mold, Pusan Polytechnic collage) ;
  • Lim Uh-Joh (Department of Mechanical Engineering, Pukyong Nat. University) ;
  • Lee Jong-Rark (R&D Center, Korea Gas Safety Corporation)
  • 곽남인 (부산기능대학 금형기술과) ;
  • 임우조 (부경대학교 공과대학) ;
  • 이종락 (한국가스안전공사 연구개발실)
  • Published : 1999.12.01
Download PDF
⟨ Previous Next ⟩

Abstract

In the study, corrosion characteristics under various corrosion environments(neutral solution, acid solution), for various hinge materials(SM20C, BsC3 and STC4H), were investigated by immersion test, and the behaviour of fretting wear under atmosphere was studied. In immersion test, corrosion potential of those materials showed to be noble in the sequence of $0.5\%HNO_3$> underground water> $0.5\%\;H_2SO_4$ solution, and potential of a sole material, except BsC3, was more noble than these of mixed materials. In same material SM20C, the fretting wear loss of rotary materials increased about 1.9 times to that of moving materials, because of surface hardening by frictional force.

일반강구조물로 많이 사용되고 있는 SM20C, BsC3 및 STC4H에 대하여, 여러 가지 부식환경(지하수($6,000{\Omega}{\cdot}cm$), $0.5\%\;H_2SO_4$ 및 $0.5\%HNO_3$)침지하에서의 부식특성 및 건조상태에서의 찰과마멸특성실험에 의한 이종금속간의 찰과마멸특성을 고찰하였다. 침지시험의 경우, 이들 금속의 전위값은 $HNO_3$, 지하수, $H_2SO_4$ 순으로 크게 나타났으며, BsC3을 제외한 동재금속보다 이종금속의 전위가 높았다. 동종재인 SM20C의 마멸은 회전측의 경우가 이동측보다 약 1.9배 증가하였으며, 이는 마찰력에 의한 표면경화가 그 원인인 것으로 추측된다.