Studies on the Physical Properties of Synthetic Rubber Blends Containing Rein-forcing Fillers

보강성 충전제를 함유한 합성고무 블렌드의 물리적 특성에 관한 연구

In order to investigate the physical properties of rubber blend compound, this experiment was carried out on the cure rate, loss tangent, reinforcement and abrasion properties of S-SBR (solution styrene-butadiene rubber) blends containing silane coupled silica and E-SBR (emulsion styrene-butadiene rubber) blends containing carbon black as a model compound. E-SBR blend showed the highest total bound rubber(TBR), while S-SBR blends showed constant TBR level regardless of rubber type. Rapid cure rate was achieved when the styrene and vinyl content of rubber microstructure decreased and TBR content of rubber compounds increased. The modulus as the index of rubber reinforcement showed the linear relation with TBR content. The large amount of PICO loss was observed when the styrene and vinyl content of rubber microstructure increased, while the small amount of PICO loss was observed when the ratio of bu-tadiene increased in the S-SBR blends with silane copuled silica. The high loss tangent at $0^{\circ}C$, the low loss tangent at $60^{\circ}C$, and the large difference of loss tangent were shown in the S-SBR blends with high styrene content compared to E-SBR blend.

보강성 충전제가 첨가된 고무블렌드의 물리적 특성을 조사하기 위해 카본블랙이 첨가된 유화중합 고무블렌드와 실란이 커플링된 실리카가 첨가된 용액중합 고무블렌드의 가황특성, 점탄성특성, 내마모 및 고무보강성 평가하였다. 유화중합 고무블렌드는 가장 높은 총결합고무량을 나타냈으나, 용액중합 고무블렌드는 고무블렌드 비율에 관계없이 일정한 총결합고무량을 나타내었다. 고무의 미세구조중 비닐 및 스틸렌 함량이 낮을수록, 배합고무중 총결합고무량이 높을수록 가황속도는 빠르게 나타났으며, 고무보강성 지표인 모듈러스는 총결합고무량과 선형적인 관계를 나타냈다. 많은 PICO 손실량은 고무의 미세구조중 비닐 및 스틸렌 함량이 증가할 때 나타났으나, 적은 PICO 손실량은 실란이 커프링된 실리카를 함유한 용액중합 고무블렌드에서 부타디엔의 비율이 증가할 때 관측되었다. 용액중합 고무블렌드는 유화중합 고무블렌드에 비해 $0^{\circ}C$에서 높은 손실계수, $60^{\circ}C$에서는 낮은 손실계수를 나타내었다.